Sol-gel bioactive glass-ceramics Part I: Calcium phosphate silicate/wollastonite glass-ceramics

Treść / Zawartość
Warianty tytułu
Języki publikacji
EN
Abstrakty
EN
In this work we present experimental results about synthesis, structure evolution and in vitro bioactivity of new calcium phosphate silicate/wollastonite (CPS/W) glass-ceramics. The samples obtained were synthesized via polystep sol-gel process with different Ca/P+Si molar ratio (R). The structure of the materials obtained was studied by XRD, FTIR spectroscopy and SEM. XRD showed the presence of Ca15(PO4)2(SiO4)6, β-CaSiO3 and α-CaSiO3 for the sample with R=1.89 after thermal treatment at 1200°C/2h. The XRD results are in good agreement with FTIR analysis. SEM denotes that apatite formation can be observed after soaking in simulated body fluid (SBF). [...]
Słowa kluczowe
Wydawca

Czasopismo
Rocznik
Tom
7
Numer
3
Strony
317-321
Opis fizyczny
Daty
wydano
2009-09-01
online
2009-06-21
Twórcy
  • Department of Chemical Technology, University of Chemical Technology and Metallurgy, 1756, Sofia, Bulgaria, l_radev@abv.bg
  • Department of Chemical Technology, University of Chemical Technology and Metallurgy, 1756, Sofia, Bulgaria
  • Department of Chemical Technology, University of Chemical Technology and Metallurgy, 1756, Sofia, Bulgaria
  • Department of Chemical Technology, University of Chemical Technology and Metallurgy, 1756, Sofia, Bulgaria
Bibliografia
  • [1] J.C. Merry, et al., J. Mater. Sci.: Mater. Med. 9, 779 (1998) http://dx.doi.org/10.1023/A:1008975507498[Crossref]
  • [2] I.R. Gibson, et al., J. Mater. Sci.: Mater. Med. 12, 799 (2000) http://dx.doi.org/10.1023/A:1008905613182[Crossref]
  • [3] A. Clifford, R. Hill, J. Non.-Cryst. Solids 196, 346 (1996) http://dx.doi.org/10.1016/0022-3093(95)00611-7[Crossref]
  • [4] Z. Feng, Y. Liao, M. Ye, J. Mater. Sci.: Mater. Med. 16, 417 (2005) http://dx.doi.org/10.1007/s10856-005-6981-8[Crossref]
  • [5] R. Morrissey, L.M. Rodriguez-Lorenzo, K.A. Gross, J. Mater. Sci.: Mater. Med. 16, 387 (2005) http://dx.doi.org/10.1007/s10856-005-6976-5[Crossref]
  • [6] E.M. Carlisle, Science 167, 179 (1970) http://dx.doi.org/10.1126/science.167.3916.279[Crossref]
  • [7] E.M. Carlisle, Calc. Tissue Int. 33, 27 (1981) http://dx.doi.org/10.1007/BF02409409[Crossref]
  • [8] M. Vallet-Regi, D. Arcos, J. Mater. Chem. 15, 1509 (2005) http://dx.doi.org/10.1039/b414143a[Crossref]
  • [9] Y-J. Lee, et al., J. Korean Ceram. Soc 40, 1096 (2003) [Crossref]
  • [10] A.J. Ruys, J. Aust. Ceram. Soc. 29, 71 (1993)
  • [11] S.R. Kim, et al., Key Eng. Mater. 218, 85 (2002) http://dx.doi.org/10.4028/www.scientific.net/KEM.218-220.85[Crossref]
  • [12] D. Arcos, J. Rogrigues-Carvajal, M. Vallet-Regi, Solid. State. Sci. 6, 987 (2004) http://dx.doi.org/10.1016/j.solidstatesciences.2004.05.001[Crossref]
  • [13] F. Barba, P. Callejas, J. Mater. Sci. 41, 5227 (2006) http://dx.doi.org/10.1007/s10853-006-0440-x[Crossref]
  • [14] M. Sayer, et al., Biomaterials 24, 369 (2003) http://dx.doi.org/10.1016/S0142-9612(02)00327-7[Crossref]
  • [15] A.M. Pietak, M. Sayer, M.J. Stott, J. Mater. Sci. 39, 2443 (2004) http://dx.doi.org/10.1023/B:JMSC.0000020008.76515.bd[Crossref]
  • [16] J.W. Reid, et al., Biomaterials 26, 2887 (2005) http://dx.doi.org/10.1016/j.biomaterials.2004.09.005[Crossref]
  • [17] H.F. Chappell, P.D. Bristowe, J. Mater. Sci.: Mater. Med. 18, 289 (2007) http://dx.doi.org/10.1007/s10856-006-0001-5[Crossref]
  • [18] A.M. Pietak, et al., Biomaterials 28, 4023 (2007) http://dx.doi.org/10.1016/j.biomaterials.2007.05.003[Crossref]
  • [19] Th. Levantouri, C. Bunacin, V. Perdikatsis, Biomaterials 24, 4205 (2003) http://dx.doi.org/10.1016/S0142-9612(03)00333-8[Crossref]
  • [20] F. Balas, J. Perez-Pariente, M. Vallet-Regi, J. Biomed. Mater. Res. 66A, 364 (2003) http://dx.doi.org/10.1002/jbm.a.10579[Crossref]
  • [21] C.M. Botelho, et al., J. Mater. Sci: Mater. Med. 13, 1123 (2002) http://dx.doi.org/10.1023/A:1021177601899[Crossref]
  • [22] N. Patel, et al., J. Mater. Sci: Mater. Med. 13, 1199 (2002) http://dx.doi.org/10.1023/A:1021114710076[Crossref]
  • [23] J. Vandiver, et al., J. Biomed. Mater. Res. 78A, 352 (2006) http://dx.doi.org/10.1002/jbm.a.30737[Crossref]
  • [24] I.R. Gibson, S.M. Best, W. Bonfield, J. Biomed. Mater. Res. 44, 422 (1999) http://dx.doi.org/10.1002/(SICI)1097-4636(19990315)44:4<422::AID-JBM8>3.0.CO;2-#[Crossref]
  • [25] E.S. Thian, et al., J. Mater. Sci. 41, 709 (2006) http://dx.doi.org/10.1007/s10853-006-6489-8[Crossref]
  • [26] E.S. Thian, et al., Biomaterials 27, 2692 (2006) http://dx.doi.org/10.1016/j.biomaterials.2005.12.019[Crossref]
  • [27] T. Kokubo, et al., Bull. Inst. Chem. Res., Kyoto Univ. 60, 260 (1980)
  • [28] J.Y. Rho, R.B. Ashman, C.H. Turner, J. Biomech. 26, 111 (1993) http://dx.doi.org/10.1016/0021-9290(93)90042-D[Crossref]
  • [29] A. Calver, R.G. Hill, A. Stamboulis, J. Mater. Sci. 39, 2601 (2004) http://dx.doi.org/10.1023/B:JMSC.0000020038.79675.0f[Crossref]
  • [30] J.A. Juhasz, et al., J. Mater. Sci: Mater. Med. 14, 489 (2003) http://dx.doi.org/10.1023/A:1023499728588[Crossref]
  • [31] P. Siriphanon, et al., J. Eur. Ceram. Soc. 22, 511 (2002) http://dx.doi.org/10.1016/S0955-2219(01)00301-6[Crossref]
  • [32] X. Liu, C. Ding, Z. Wang, Biomaterials 22, 2007 (2001) http://dx.doi.org/10.1016/S0142-9612(00)00386-0[Crossref]
  • [33] P.N. De Aza, et al., J. Microscopy 197, 60 (2000)
  • [34] P.N. De Aza, et al., J. Am. Ceram. Soc. 89, 2619 (2006) http://dx.doi.org/10.1111/j.1551-2916.2006.01108.x[Crossref]
  • [35] R.G. Hill, M. Patel, D.J. Wood, in: W. Bonfield, G.W. Castings, K.E. Tanner (Eds), Bioceramics, vol. 4 (Buttrerworth-Heinemann, London, 1991) 79
  • [36] R. Hill, D. Wood, J. Mater. Sci: Mater. Med. 6, 311 (1995) http://dx.doi.org/10.1007/BF00120298[Crossref]
  • [37] B. Samuneva, et al., J. Sol-Gel Sci. and Technol. 13, 255 (1998) http://dx.doi.org/10.1023/A:1008647404796[Crossref]
  • [38] B. Samuneva, et al., J. Sol-Gel Sci. and Technol. 26, 1203 (2003) http://dx.doi.org/10.1023/A:1020716404034[Crossref]
  • [39] B. Samuneva, et al., J. Sol-Gel Sci. and Technol. 26, 273 (2003) http://dx.doi.org/10.1023/A:1020767603299[Crossref]
  • [40] V. Hristov, et al., in: E. Balabanova, I. Dragieva (Eds.), Eight Workshop on Nanostructured Materials Application and Innovation Transfer, Sofia, Bulgaria (Nanoscience & Nanotechnology 7, 2007) 235
  • [41] K. Hata, N. Ozawa, T. Kokubo, J. Ceram. Soc. Jpn. 109(6), 489 (2001) [Crossref]
  • [42] W.G. Mumme, et al., N. Jb. Miner. Abh. 169, 35 (1995)
  • [43] X.W. Li, H. Yasuda, Y. Umacoshi, J. Mater. Sci: Mater. Med. 17, 573 (2006) http://dx.doi.org/10.1007/s10856-006-8942-2[Crossref]
  • [44] H-S. Ryu, et al., J. Mater. Res. 20, 1154 (2005) http://dx.doi.org/10.1557/JMR.2005.0144[Crossref]
  • [45] I. Rehman, W. Bonfield, J. Mater. Sci.: Mater. Med. 8, 1 (1997) http://dx.doi.org/10.1023/A:1018570213546[Crossref]
  • [46] S. Agathopoulos, et al., J. Non.-Cryst. Solids 352, 322 (2006) http://dx.doi.org/10.1016/j.jnoncrysol.2005.12.003[Crossref]
  • [47] A. Martines, I. Izquierdo-Barba, M. Vallet-Regi, Chem. Mater. 12, 3080 (2000) http://dx.doi.org/10.1021/cm001107o[Crossref]
  • [48] M. Jokinen, et al., J. Sol-Gel. Sci. Techn. 12, 159 (1998) http://dx.doi.org/10.1023/A:1008642117227[Crossref]
  • [49] P. Richet, B.O. Mysen, J. Ingrin, Phys. Chem. Minerals 25, 401 (1998) http://dx.doi.org/10.1007/s002690050130[Crossref]
  • [50] V. Swanmy, L. Dubrovinsky, F. Tutti, J. Am. Ceram. Soc. 80, 2237 (1997) http://dx.doi.org/10.1111/j.1151-2916.1997.tb03113.x[Crossref]
  • [51] S.V. Dorozkin, J. Am. Ceram. Soc. 90, 244 (2007) http://dx.doi.org/10.1111/j.1551-2916.2006.01368.x[Crossref]
  • [52] M. Vallet-Regi, D. Ramila, Chem. Mater. 12, 961 (2000) http://dx.doi.org/10.1021/cm991110b[Crossref]
  • [53] N. Nagai, T. Saeki, T. Kokubo, J. Am. Ceram. Soc. 73, 1456 (1990) http://dx.doi.org/10.1111/j.1151-2916.1990.tb05228.x[Crossref]
  • [54] P. Li, et al., J. Am. Ceram. Soc. 75, 2094 (1992) http://dx.doi.org/10.1111/j.1151-2916.1992.tb04470.x[Crossref]
Typ dokumentu
Bibliografia
Identyfikatory
Identyfikator YADDA
bwmeta1.element.-psjd-doi-10_2478_s11532-009-0022-2
JavaScript jest wyłączony w Twojej przeglądarce internetowej. Włącz go, a następnie odśwież stronę, aby móc w pełni z niej korzystać.