Synthesis and characterization of nanosized NiO2 and NiO using Triton® X-100

• Autorzy: Mohammad Kooti , Mehdi Jorfi
• Języki publikacji: EN

Abstrakty

EN

Nanosized NiO2 particles with an average diameter of 15 nm are prepared by treating of Ni(NO3)2 · 6H2O with an aqueous solution of KClO in the presence of Triton® X-100. This black fine powder of nickel peroxide was characterized by XRD diffraction, energy dispersive spectroscopy (EDS) and scanning electron microscopy (SEM). The as-prepared NiO2 can be easily transformed to nanosized NiO merely by washing it with acetone. The obtained NiO has an average diameter of 40 nm and was characterized by the same means used for NiO2. The nanoparticles of NiO2 and NiO were obtained in high yields and purities. [...]

Słowa kluczowe

EN

Nanosized; NiO2; NiO; Triton® X-100

• Czasopismo: Open Chemistry
• Rocznik: 2009
• Tom: 7
• Numer: 1
• Strony: 155-158

Daty

wydano

2009-03-01

online

2008-12-23

Twórcy

autor

Mohammad Kooti

• Department of Chemistry, College of Science, Shahid Chamran University, 65355-141, Ahvaz, Iran,

autor

Mehdi Jorfi

• Department of Chemistry, College of Science, Shahid Chamran University, 65355-141, Ahvaz, Iran

Bibliografia

• [1] C. Wieser, C.B. Dieleman, D. Matt, Coord. Chem. Rev. 165, 93 (1997)
• [2] B. Moulton, M.J. Zaworotko, Chem. Rev. 101, 1629 (2001) http://dx.doi.org/10.1021/cr9900432[Crossref]
• [3] S. Kitagawa, R. Kitaura, S.I. Naro, Angew. Chem. Int. Ed. 43, 2334 (2004) http://dx.doi.org/10.1002/anie.200300610[Crossref]
• [4] J.W. Ko, K.S. Min, M.P. Suh, Inorg. Chem. 41, 2151 (2002) http://dx.doi.org/10.1021/ic011281u[Crossref]
• [5] X. Li, R. Cao, Q. Sun, Q. Shi, D.Q. Yuan, D.F. Sun, W.H. Bi, M.E. Hong, Cryst. Groth Des. 4, 255 (2004) http://dx.doi.org/10.1021/cg034156x[Crossref]
• [6] C.N.R. Rao, N. Srinibasan, R. Vaidhyanathan, Angew. Chem. Int. Ed. 43, 1466 (2004) http://dx.doi.org/10.1002/anie.200300588[Crossref]
• [7] D. Shigehito, K. Akamatsu, T. Yano, M. Mizuhata, A. Kajinami, J. Mater. Chem. 818, 1865 (1998)
• [8] Y. Wang, Q.Z. Qin, J. Electrochem. Soc. 149, A873 (2002) http://dx.doi.org/10.1149/1.1481715[Crossref]
• [9] C. Wang, Y. Hu, Y. Quian, G. Zhao, Nanostruct. Mater. 7, 421 (1996) http://dx.doi.org/10.1016/0965-9773(96)00016-5[Crossref]
• [10] I.W. Lenggoro, Y. Itoh, N. Iida, K. Okuyama, Mater. Res. Bull. 38, 1819 (2003) http://dx.doi.org/10.1016/j.materresbull.2003.08.005[Crossref]
• [11] F. Svegl, B. Orel, I.G. Svegl, V. Kaucic, Electrochim. Acta 45, 4359 (2000) http://dx.doi.org/10.1016/S0013-4686(00)00543-0[Crossref]
• [12] D.H. Chen, C.H. Hsieh, J. Mater. Chem. 12, 2412 (2002) http://dx.doi.org/10.1039/b200603k[Crossref]
• [13] S.W. Oh, H.J. Bang, Y.C. Bae, Y.K. Sun, J. Power Sources 173 (2007)
• [14] X. Chen, X. Hu, J. Feng, Nanostruct. Mater. 6, 309 (1995) http://dx.doi.org/10.1016/0965-9773(95)00059-3[Crossref]
• [15] B. Pejova, T. Kocareva, M. Najadoski, I. Grozdanor, Appl. Surf. Sci. 165, 271 (2000) http://dx.doi.org/10.1016/S0169-4332(00)00377-9[Crossref]
• [16] W. Xing, F. Li, Z.F. Yan, G.Q. Lu, J. Power Sources 134, 324 (2004) http://dx.doi.org/10.1016/j.jpowsour.2004.03.038[Crossref]
• [17] Y. Lin, T. Xie, B. Cheng, B. Geng, L. Zhang, Chem. Phys. Lett. 28, 521 (2003) http://dx.doi.org/10.1016/j.cplett.2003.09.066[Crossref]
• [18] K.C. Liu, M.A. Anderson, J. Electrochem. Soc. 143, 124 (1996) http://dx.doi.org/10.1149/1.1836396[Crossref]
• [19] S.F. Wang, L.Y. Shi, X. Feng, S.R. Ma, Mater. Lett. 61, 1549 (2007) http://dx.doi.org/10.1016/j.matlet.2006.07.076[Crossref]
• [20] X. Deng, Z. Chen, Matter. Lett. 58, 276 (2004) http://dx.doi.org/10.1016/S0167-577X(03)00469-5[Crossref]
• [21] K. Nakagawa, R. Konake, T. Nakata, J. Org. Chem. 17, 1797 (1962)
• [22] M.V. George, K.S. Balachandran, Chem. Rev. 75, 491 (1975) http://dx.doi.org/10.1021/cr60296a004[Crossref]
• [23] H. Ji, T. Wang, M. Zhang, Y. She, L. Wang, Appl. Catal. A: General 282, 25 (2005) http://dx.doi.org/10.1016/j.apcata.2004.11.043[Crossref]
• [24] J. M. Grill, J.W. Ogle, S. A. Miller, J. Org. Chem. 71, 9291 (2006) http://dx.doi.org/10.1021/jo0612574[Crossref]
• [25] Y. Sun, B. Gaten, B. Mayers, V. Xia, Nano Lett. 2, 167 (2002)
• [26] C. Faure, C. Delmas, M. Fouassier, J. Power Sources 35, 279 (1991) http://dx.doi.org/10.1016/0378-7753(91)80112-B[Crossref]
• [27] T. Ahmad, K.V. Ramanujachary, S.E. Lofland, A.K. Ganguli, Solid State Sci. 8, 425 (2006) http://dx.doi.org/10.1016/j.solidstatesciences.2005.12.005[Crossref]

Identyfikatory

DOI

10.2478/s11532-008-0077-5