Microstructure and Thermoelectric Properties of Doped FeSi2 with Addition of B4C Nanoparticles

Dąbrowski Franciszek, Ciupiński Łukasz, Zdunek Joanna, Chromiński Witold, Kruszewski Mirosław, Zybala Rafał, Michalski A., Kurzydłowski Krzysztof J.

Archives of Metallurgy and Materials

|

2021

|

Vol. 66, iss. 4

1157--1162

EN

β-FeSi2 with the addition of B4C nanoparticles was manufactured by sintering mechanically alloyed Fe and Si powders with Mn, Co, Al, P as p and n-type dopants. The consolidated samples were subsequently annealed at 1123 K for 36 ks. XRD analysis of sinters after annealing confirmed nearly full transformation from α and ε into thermoelectric β-FeSi2 phase. SEM observations of samples surface were compliant with the diffraction curves. TEM observations allowed to depict evenly distributed B4C nanoparticles thorough material, with no visible aggregates and establish grain size parameter d2 < 500 nm. All dopants contributed to lower thermal conductivity and Seebeck coefficient, with Co having strongest influence on increasing electrical conductivity in relation to reference FeSi2. Combination of the addition of Co as dopant and B4C nanoparticles as phonon scatterer resulted in dimensionless figure of merit ZT reaching 7.6 × 10-2 at 773 K for Fe0.97Co0.03Si2 compound. Comparison of the thermoelectric properties of examined sinters to the previously manufactured of the same stoichiometry but without B4C nanoparticles revealed theirs overall negative influence.

2

Wybrane aspekty badań eksploatacyjnych autonomicznych zasilaczy dla zastosowań specjalnych

Paziewski P., Watral Z., Michalski A.

Przegląd Elektrotechniczny

|

2018

|

R. 94, nr 9

113--116

PL

Przedstawiony artykuł dotyczy zasad doboru i badań temperaturowych akumulatorowych źródeł energii elektrycznej przeznaczonych do pracy w warunkach terenowych. Zaproponowano metodykę doboru rodzaju akumulatora i określania jego niezbędnej pojemności. Wyniki przeprowadzonych badań potwierdziły prawidłowość przyjętych rozwiązań, zaś badania temperaturowe pozwoliły ograniczyć pierwotnie przewidywaną pojemność.

EN

The presented article concerns the principles of selection and temperature testing of battery-powered electric energy sources intended for work in field conditions. The methodology of choosing the type of battery and determining its necessary capacity has been proposed. The results of the conducted tests confirmed the correctness of the adopted solutions, while temperature tests allowed to limit the initially anticipated capacity.

3

Synthesis and characterization of high-molar-mass star-shaped poly(l-lactide)s

Michalski A., Łapienis G.

Polimery

|

2018

|

T. 63, nr 7-8

488--494

EN

The synthesis of high-molar-mass linear and 6-arm star-shaped poly(l-lactide)s(PLLA’s) is presented. Dipentaerythritol and benzyl alcohol were used asinitiators and Sn(Oct)2 was applied asa catalyst in the ring-opening polymerization (ROP) of l-lactide (l-LA) carried out at 130 °C. The prepared PLLA’s were characterized by SEC (size exclusion chromatography), 1H NMR (proton nuclear magnetic resonance spectroscopy), DSC (differential scanning calorimetry), and TGA (thermogravimetric analysis). The structure of the obtained star-shaped polymers was confirmed by comparison of the radii of gyration (Rg) determined by SEC for the linear and star macromolecules. The thermal properties of PLLA’s were shown for the wide range of molar masses. Additionally, it was confirmed that Irganox stabilizer has an influence on the thermal stability of PLLA’s.

PL

Przedstawiono syntezę liniowych i 6-ramiennych gwiaździstych poli(l-laktydów)(PLLA) o dużych masach molowych. Polimeryzację z otwarciem pierścienia (ROP) l-laktydu(l-LA) inicjowaną dipentaerytrytem oraz alkoholem benzylowym prowadzono w temperaturze130 °C wobec Sn(Oct)2 jako katalizatora. Otrzymane PLLA scharakteryzowano za pomocą SEC (chromatografia żelowa), 1HNMR (spektroskopia magnetycznego rezonansu jądrowego), DSC (różnicowa kalorymetria skaningowa) i TGA (analiza termograwimetryczna). Strukturę otrzymanych polimerów gwiaździstych potwierdzono przez porównanie wyznaczonych w SEC promieni bezwładności (Rg) dla gwiaździstych iliniowych makrocząsteczek. Właściwości termiczne PLLA przedstawiono dla szerokiego zakresu mas molowych. Dodatkowo potwierdzono, że stabilizator Irganox ma wpływ na stabilność termiczną PLLA.

4

Tekst drukowany czy wyświetlany? O zaletach druku w dobie wyświetlaczy

Michalski A., Rogaczewska M., Stopa M.

Optyka

|

2018

|

Nr 1

57--57

PL

Postęp technologiczny spowodował powszechną cyfryzację różnych form przekazu – nie ominął także tekstu. Obecnie czytelnik może korzystać z publikacji w formie drukowanej na papierze, prezentowanej na urządzeniach wykorzystujących technologię atramentu elektronicznego lub na wyświetlaczach ciekłokrystalicznych. Podjęto zatem próbę oceny, która z tych form najmniej obciąża narząd wzroku. Mimo popularności cyfrowych form okazało się, że tradycyjny wydruk jest najbardziej komfortowym sposobem czytania.

EN

The technological development resulted in widespread digitalization, including books. Nowadays, readers can use printed text, devices with electronic ink technology or liquid crystal display screens. Researchers evaluated which form of text presentation causes less eye fatigue. Despite the popularity of digital text devices, the traditional print is still the most comfortable way of reading.

5

Omówienie metod zmniejszania rozwoju krótkowzroczności

Michalski A., Maleszka-Kurpiel M., Rogaczewska M., Stopa M.

Optyka

|

2018

|

Nr 4

34--36

PL

Istotność kontroli krótkowzroczności jest związana z rosnącym odsetkiem światowej populacji obarczonej tą wadą wzroku, a jest ona jednym z czynników ryzyka wystąpienia innych chorób oczu. W licznych pracach poddawano analizie wpływ różnych metod optycznych i farmakologicznych na spowolnienie progresji krótkowzroczności. Stosowano zarówno korekcję okularową i soczewkami kontaktowymi o konstrukcjach dwu i wieloogniskowych, jak i ortokeratologię. Wśród leków badano przede wszystkim wpływ różnych stężeń atropiny na zahamowanie progresji krótkowzroczności. Rzadziej opisywano zastosowanie innych leków, np. pirenzepiny. Za najbardziej skuteczne metody, powodujące największe spowolnienie zwiększania się krótkowzroczności, uznano zastosowanie soczewek kontaktowych modyfikujących obwodowe rozogniskowanie, soczewek ortokeratologicznych oraz użycie atropiny, przede wszystkim w niskich stężeniach. W licznych opracowaniach podkreślono też szkodliwy – przyspieszający narastanie krótkowzroczności – wpływ niedokorygowania. Podnosi się też możliwy hamujący wpływ na progresję tej wady refrakcji czasu spędzanego na zewnątrz pomieszczeń, czyli na świeżym powietrzu. Aby osiągnąć sukces w kontroli krótkowzroczności, należy wcześnie wykryć wadę, skorygować ją w pełni i zastosować najbardziej skuteczne metody zahamowania jej progresji.

EN

The importance of myopia control is associated with a growing percentage of myopes in the population. This refractive error can be a risk factor for other eye diseases. Many researchers studied the influence of various optical and pharmacological strategies for the reduction of myopia advancement. Glasses, bi- and multifocal contact lenses use, and orthokeratology were analyzed. The pharmacological approach included mainly the instillation of different dilutions of atropine and less frequently the use of pirenzepine drops. The wear of periph- eral defocus-modifying contact lenses, orthokeratology, and low concentration atropine are regarded as the most effective strategies. Many researchers high- lighted the harmful effect of under-correction because it could cause the myopia progression. The outdoor activities can have a possible inhibitory impact on the refractive error advancement. To sum up, the success of myopia control depends on three factors: the early recognition of the refractive error, its full correction, and the selection of the most effective method, which slows its progression.

6

Program „Czyste powietrze”

Michalski A., Mazur S.

Energia i Recykling : gospodarka obiegu zamkniętego

|

2018

|

nr 10

18

PL

Z Arturem Michalskim, wiceprezesem Zarządu Narodowego Funduszu Ochrony Środowiska i Gospodarki Wodnej, rozmawia Szymon Mazur.

7

Stereocomplexation of polylactides containing ionic liquid end-groups

Biedroń T., Michalski A., Biela T., Kubisa P.

Polimery

|

2017

|

T. 62, nr 4

254--261

EN

Linear and cyclic oligomers of epichlorohydrin were synthesized and converted by reaction with N-methylimidazole into linear or cyclic derivatives fitted with imidazolium ionic liquid groups. These oligomers containing hydroxyl groups were used as macroinitiators of cationic polymerization of L- and D-lactide. Two types of products were obtained: linear polylactides (PLA's) containing a few ionic liquid groups at the chain end and star PLA's containing a few ionic liquid groups at the core. The enantiomeric forms of PLA, poly(L-lactide) (PLLA) and poly(D-lactide) (PDLA) were used for stereocomplexation studies following earlier observation that if PLLA and PDLA containing one imidazolium ionic liquid group at the chain end are mixed in 1,4-dioxane solution, stereocomplex precipitates spontaneously in form of uniform microspheres. In a present contribution it is shown that if more than one ionic liquid group is introduced at the chain ends of PLLA and PDLA, morphology of precipitated stereocomplex is similar to that observed for PLA's fitted with one ionic liquid group but microspheres are slightly less regular. When few ionic liquid groups are present at the core of star PLLA no specific morphology is observed for precipitating stereocomplex with linear PDLA fitted with C4H9O- group. Only when end-groups able to interacting with each other are introduced, specific morphology appears. With ionic liquid end-groups in linear component, stereocomplex precipitates in form of irregular granules while with strongly interacting ureidopirymidine end-groups, microspheres, although not very regular, are formed. These results indicate that well defined morphology (regular spherical particles) is observed when interacting groups are present at the freely moving chain ends but not, when the same groups are embedded and immobilized at the core of star polymers and through it probably are hidden inside polymer random coil.

PL

Otrzymano liniowe i cykliczne oligomery epichlorohydryny, następnie grupy chlorometylowe przekształcono – w reakcji z N-metyloimidazolem – w imidazoliowe, analogiczne do grup występujących w cieczach jonowych. Oligomery zawierające grupy hydroksylowe zastosowano jako makroinicjatory kationowej polimeryzacji L- i D-laktydu, w wyniku której uzyskano dwa rodzaje produktów: liniowe polimery laktydu (PLA) z udziałem kilku grup cieczy jonowej na jednym zkońców łańcucha oraz gwiaździste polimery laktydu zawierające kilka grup cieczy jonowej w centrum gwiaździstej makrocząsteczki. Enancjomeryczne formy PLA: poli(L-laktyd) (PLLA) i poli(D-laktyd) (PDLA) zastosowano do wytworzenia stereokompleksów. Wykazano, że jeśli na końcu łańcucha znajduje się więcej niż jedna grupa cieczy jonowej, morfologia wytrącającego się stereokompleksu jest zbliżona do morfologii obserwowanej w wypadku obecności tylko jednej grupy cieczy jonowej, ale mikrosfery są mniej jednorodne. Wyniki wskazują, że regularne mikrosfery powstają jeśli grupy zdolne do wzajemnych oddziaływań znajdują się na końcach liniowych makrocząsteczek, nie powstają natomiast wtedy, gdy grupy te znajdują się w centrum gwiaździstej makrocząsteczki i są otoczone jej ramionami.

8

Czy zastosowanie korekcji okularami wieloogniskowymi zwiększa ryzyko wystąpienia urazów w wyniku upadku

Rogaczewska M., Michalski A., Stopa M.

Optyka

|

2017

|

Nr 5

56--58

PL

Jedną ze zmian następujących w organizmie człowieka wraz z jego starzeniem się jest zmniejszanie się amplitudy akomodacji utrudniające obserwację położonych blisko przedmiotów. Konieczne staje się zastosowanie u prezbiopów korekcji uwzględniającej dodatek do bliży – często są to okulary z soczewkami dwuogniskowymi lub progresywnymi. Osoby w wieku podeszłym ulegają też znamiennie częściej urazom w wyniku upadków. Podjęto zatem próbę rozważenia, czy określony rodzaj korekcji okularowej zastosowanej u osoby starszej może zmodyfikować ryzyko wystąpienia u niej upadku, a tym samym obrażeń. Choć okulary wieloogniskowe poprawiają komfort funkcjonowania we współczesnym świecie, to jednak zastosowanie korekcji jednoogniskowej zmniejsza ryzyko upadku podczas poruszania się po przestrzeni miejskiej. W przypadku korekcji dwuogniskowej - ryzyko to będzie największe. Należy zatem indywidualnie rozważyć wybór odpowiedniej korekcji okularowej dla danej osoby.

EN

The aging process in humans concerns i.a. changes in a crystalline lens, namely its amplitude of accommodation decreases. Thus, presbyopic patients have difficulties when focusing on close objects and they need to wear glasses for near vision activities. They often use bifocal and multifocal lenses. Fall-related injuries appear also more frequently among elderly people. It was considered, if wearing particular kind of lenses may influence fall and injury risk in older adults. Although the multifocal glasses improve living comfort in a modern world, single lens glasses reduce the risk of falls when walking outside, whereas bifocal lenses – amplify it. Therefore, every patient should be individually evaluated for the most appropriate glasses .

9

Aspekty techniczne prefabrykacji betonowej w budownictwie ogólnym

Adamczewski G., Deskur B., Michalski A., Chyła T., Stasieńko B., Marzec G., Łuczak M.

Materiały Budowlane

|

2017

|

nr 9

84--90

10

Properties of Ni3Al–diamond composites sintered by Pulsed Plasma Sintering

Cymerman K., Michalski A., Pakieła Z., Moszczyńska D.

Inżynieria Materiałowa

|

2017

|

Vol. 38, nr 2

88--92

EN

This study presents properties of Ni3Al–diamond composites sintered by Pulsed Plasma Sintering (PPS) with the participation of SHS reaction (Self-propagating High-temperature Synthesis). Ni3Al–diamond sinters were produced using Ni:Al (3:1 at.) powder mixtures with addition of 30 vol. % of diamond with grain size ranging from 16 to 60 μm. The sintering process was performed at 1000°C in 5 minutes under load of 100 MPa. Obtained sinters have above 99% theoretical density and show fine crystalline microstructure with relatively uniformed diamond particles, what can be observed in SEM images of polished and fracture surface. The fractures are brittle and have the intergranular character. The X-ray phase examinations have shown that each sinter contains Ni3Al, diamond and Ni3C. The sinters hardness was tested by the Vickers method and oscillated between 580 and 650 HV5. The average grain size of Ni3Al matrix in obtained composites ranged from 2.6 to 3.8 μm.

PL

Rosnące zapotrzebowanie na różnego rodzaju narzędzia skrawające skłania do poszukiwania nowszych i bardziej wytrzymałych materiałów. W przypadku narzędzi diamentowych, tj. takich z dyspersyjnie rozmieszczonymi cząstkami diamentu, bardzo ważną rolę odgrywa osnowa. Najczęściej stosowaną osnową są związki na bazie kobaltu i żelaza. Jednak ze względu na cenę, a przede wszystkim rakotwórczy wpływ na zdrowie, dąży się do wyeliminowania kobaltu. Materiałem mogącym go zastąpić mogą być związki z układu Ni–Al. Dużym zainteresowaniem naukowców w ostatnich latach cieszą się spiekane kompozyty Ni3Al z dodatkiem cząstek TiB2, TiC lub SiC.

11

The impact of postglacial palaeoenvironmental changes on the properties of sediments in the kettle hole at Jurki (NE Poland)

Karasiewicz T. M., Hulisz P., Noryśkiewicz A. M., Stachowicz-Rybka R., Michalski A., Dąbrowski M., Gamrat W. W.

Geological Quarterly

|

2017

|

Vol. 61, No. 2

319--333

EN

This research is focused on a small kettle hole located within the Morąg moraines (Iława Lake District, NE Poland). The study objective was to determine the impact of palaeoenvironmental changes in sedimentation and properties of sediments filling the bottom of the kettle hole. Sedimentological, geochemical, and palaeobotanical studies enabled us to distinguish several development phases of the kettle hole, and cluster analysis performed on physicochemical data yielded seven local geochemical zones (JuI/I to JuI/VII). The beginning of biogenic sedimentation in the conditions of a small water body, functioning in the Late Glacial period (4.20–4.10 m), was determined on the basis of palaeobotanical research. Sediments deposited in the lake during its further evolution were rich in microelements such as Ca, Na, Mg, and K, and to a smaller extent – Fe and Mn (JuI/I–III local geochemical zones). The Late Glacial lacustrine period ended with the accumulation of very silty, pollen-free gyttja, with a stratigraphic hiatus (JuI/IV, 3.40–3.20 m). The sediments were enriched with SiO2ter, which indicates an increased rate of slope erosion, and concretions of Fe-Mn occurring below this layer (JuIII) provide evidence for lowering of the water level and even desiccation. In the Holocene, the lacustrine period ended with the accumulation of coarse detrital gyttja (3.20–2.60 m). Palaeobotanical data indicate that the next group of sediments were deposited in the Late Subboreal and Subatlantic periods (2.60–0.0 cm, JuI/V–VII; sedge peat). Their properties were varied and related to hydrologic conditions, limited denudation, and vegetation succession. There was also a significant change in the trophic conditions of the water and consequently in the sediments of the kettle hole, which changed during the lacustrine period from basic to acid, and strongly acid in the surface layer. This reaction may be related to a change in the water regime as well as to human impact in the environment, which led to the colonization of the peat bog by Sphagnum moss.

12

Konstrukcja węzła bezprzewodowej sieci czujnikowej wykorzystującego Energy Harvesting

Dziadak B., Makowski Ł., Michalski A.

Przegląd Elektrotechniczny

|

2016

|

R. 92, nr 11

63--66

PL

W artykule przedstawione są założenia oraz wyniki prac, dotyczące budowy energetycznie autonomicznego węzła pomiarowego bezprzewodowej sieci czujnikowej. Elementem centralnym węzła jest mikrokontroler MSP430 cechujący się bardzo niskim zużyciem energii modem radiowy pracujący w paśmie 2,4 GHz oraz blok energetyczny składający się z ogniw fotowoltaicznych oraz termogeneratora TEG wraz z układem zarządzani i magazynowania energii oraz blok sensorów konfigurowalny w zależności od potrzeb. W trybie przesłania informacji pomiarowej raz na minutę węzeł potrzebuje 40 mJ energii co jest możliwe do zgromadzenia w ciągu 57 sekund przy zastosowaniu amorficznego panelu solarnego o wymiarach 3050 mm pracującego w warunkach oświetlenia na poziomie 900 lux.

EN

Outline of construction of new, autonomous wireless sensor node is presented in this paper. Central point of the node is built around MSP430FR microcontroller that is characterised with extremely low energy consumption. Additional elements of the node are radio communication module working in 2.4 GHz band, power supply section consisting of photovoltaic panels and thermoelectric generator with necessary regulators and sensors block configured due to specific needs. During typical measurement process node need 40 mJ per minute, what can be obtained per 57 seconds, using amorphous solar panel 3050 mm operating on 900 lux insulation.

13

Development of the substitutive circuit for the electromagnetic flowmeter

Brykalski B., Jakubowski J., Michalski A., Watral Z.

Przegląd Elektrotechniczny

|

2016

|

R. 92, nr 11

158--161

EN

The paper presents the results of measurements of the electrical properties of the sensor in the electromagnetic flowmeter. The RC network and its parameters were identified for it. The influence of them on the LS flow velocity estimation in the pulse mode was also examined by simulation. The results showed that using oscillatory excitation gives erroneous results of estimation.

PL

W artykule przedstawiono wyniki pomiarów własności elektrycznych czujnika w przepływomierzu elektromagnetycznym. Wyznaczono dla niego układ zastępczy RC oraz dokonano identyfikacji parametrów. Przebadano również metodą symulacyjną ich wpływ na estymację LS prędkości przepływu w trybie impulsowym. Wyniki dowodzą, że wykorzystanie pobudzania oscylacyjnego jest źródłem błędów estymacji.

14

Survey of Energy Harvesting Systems for Wireless Sensor Networks in Environmental Monitoring

Dziadak B., Makowski Ł., Michalski A.

Metrology and Measurement Systems

|

2016

|

Vol. 23, nr 4

495--512

EN

Wireless Sensor Networks (WSNs) have existed for many years and had assimilated many interesting innovations. Advances in electronics, radio transceivers, processes of IC manufacturing and development of algorithms for operation of such networks now enable creating energy-efficient devices that provide practical levels of performance and a sufficient number of features. Environmental monitoring is one of the areas in which WSNs can be successfully used. At the same time this is a field where devices must either bring their own power reservoir, such as a battery, or scavenge energy locally from some natural phenomena. Improving the efficiency of energy harvesting methods reduces complexity of WSN structures. This survey is based on practical examples from the real world and provides an overview of state-of-the-art methods and techniques that are used to create energyefficient WSNs with energy harvesting.

15

The use of kernel estimators to determine the distribution of groundwater level

Michalski A.

Meteorology Hydrology and Water Management. Research and Operational Applications

|

2016

|

Vol. 4, Iss. 1

41--46

EN

In this paper the problem of non-parametric estimation of the probability density function for hydrological data is considered. For a given random sample X1, X2, ..., Xn we define an estimator fˆ n of the density function ƒ based on a function K of a real variable – the so-called kernel of a distribution – and a properly chosen number sequence {hn} from the interval (0, ∞). This estimator of density function of a random variable X under more general assumptions is known in the statistical literature as the Parzen-Rosenblatt estimator or the kernel estimator. The method of kernel estimation presented in the paper has been applied to determine the probability distribution of the groundwater level based on long-term measurements made in the melioration research carried out at the foothill object Długopole.

16

Analiza pracy rurociągów transportu chłodu w układach klimatyzacji kopalń

Szulc P., Skowroński M., Michalski A.

Logistyka

|

2015

|

nr 4

6042--6051, CD 2

PL

W artykule przedstawiono wyniki analizy hydraulicznej i termodynamicznej pracy rurociągów transportu chłodu w układzie klimatyzacji centralnej kopalni głębokiej. Ponieważ temperatura odsłoniętego górotworu wynosi około 47 °C, a wilgotność względna waha się w przedziale 0,75 – 0,8 system wentylacji nie jest w stanie zabezpieczyć komfortu termicznego górników, stąd konieczność stosowania układów klimatyzacyjnych. W procesie transportu wody lodowej na przodki konieczne jest zapewnienie minimalnej wartości strat ciepła. W pracy zaprezentowano wyniki symulacji oraz rezultaty badań rzeczywistych kilku wybranych rurociągów. Otrzymane wyniki analizy porównawczej wykazały konieczność stosowania współczynników poprawkowych, umożliwiających uzyskanie zbieżności wyników na odpowiednim poziomie. Tak przeprowadzone prace pozwalają zbudować model obliczeniowy, którego zastosowanie umożliwi2 optymalizację i prognozowanie reakcji układu na zmienne warunki pracy.

EN

The paper presents the results of thermal and hydraulic analysis of the pipelines of main cooling system in the mine. As the average temperature in excavation is approximately 47°C and humidity within range of 0,75–0,80 the ventilating system could not ensure proper air parameters for workers, so the other system of air–conditioning is required. The process of cool water movement should be realised with the minimum value of heat losses. In this paper the results of theoretical simulations and physical measurements were presented. Received results of comparison showed, that correction coefficients must be allied to secure proper level of convergence. The analysis allow the creation of calculation model, which application will be helpful in optimization of analysed net.

17

Wpływ wielkości cząstek diamentu na strukturę i właściwości kompozytów Ni3Al–diament wytwarzanych metodą impulsowo-plazmową

Cymerman K., Michalski A., Kulikowski K.

Inżynieria Materiałowa

|

2015

|

Vol. 36, nr 6

506--510

PL

Obecnie trwają prace nad zastąpieniem osnowy z drogiego i rakotwórczego kobaltu w kompozytach metal–diament materiałem na bazie faz międzymetalicznych z układu Ni–Al. W pracy przedstawiono wpływ wielkości cząstek diamentu na właściwości kompozytów Ni3Al–diament otrzymanych metodą impulsowo- plazmową (PPS) z udziałem reakcji SHS (Self-propagating Hight-temperature Synthesis). Do mieszaniny proszków Ni:Al w proporcji 3:1 dodano 30% obj. proszku diamentu o rozmiarze cząstek 16÷20 oraz 40÷60 μm. Następnie próbki spiekano w temperaturze 900°C przez 5 minut pod ciśnieniem prasowania 100 MPa. Otrzymane spieki wykazują gęstość względną powyżej 98% i charakteryzują się drobnokrystaliczną strukturą z równomiernie rozmieszczonymi cząstkami diamentu, co potwierdzają obserwacje powierzchni zgładów i przełomów za pomocą skaningowego mikroskopu elektronowego. Charakter przełomów jest kruchy, a mechanizm pękania międzykrystaliczny. Kompozyty Ni3Al–diament poddano także badaniu rentgenowskiej analizy fazowej, która poza fazą Ni3Al i diamentem wykazała obecność fazy Ni3C, bez względu na wielkość zastosowanego diamentu. Twardość Vickersa wynosiła 578±9 HV5 dla spieku Ni3Al–diament 16÷20 μm oraz 606±2 HV5 dla spieku Ni3Al–diament 40÷60 μm. Spieki Ni3Al–diament poddano badaniom odporności na zużycie przez tarcie metodą kula–tarcza. Zużycie kompozytów diamentowych jest znikome i praktycznie niemierzalne. Spiek z diamentem o cząstkach 40÷60 μm charakteryzował się mniejszym współczynnikiem tarcia niż spiek Ni3Al–diament 16÷20 μm. Podsumowując, wielkość cząstek diamentu zastosowanego w kompozytach Ni3Al–diament nie wpływa na mikrostrukturę. Zauważalnie zwiększają się właściwości mechaniczne (twardość, odporność na ścieranie) z zastosowaniem diamentu o większych cząstkach 40÷60 μm.

EN

There is an increasing number of research studies with aim to eliminate carcinogenic and expensive cobalt from metal–diamond composites and replace it by Ni–Al intermetallic phases. This study presents the influence of diamond particle size on the properties of Ni3Al–diamond composites sintered by Pulsed Plasma Sintering (PPS) with the participation of SHS reaction (Self-propagating High-temperature Synthesis). Ni3Al–diamond sinters were produced using Ni:Al (3:1 at.) powder mixtures with addition of 30% vol. of diamond with grain size ranging from 16 to 60 μm. The sintering process was performed at 900°C in 5 minutes under load 100 MPa. Obtained sinters have above 98% theoretical density and shows fine crystalline microstructure with relatively uniformed diamond particles, what can be observed on SEM images of polished surface and fracture. The fractures are brittle and have the intergranular character. The X-ray phase examinations have shown that each sinters contains Ni3Al, diamond and Ni3C. Hardness of the sinters was tested by the Vickers method and was 578±9 HV5 for Ni3Al–diamond 16÷20 μm sinter and 606±2 HV5 for Ni3Al–diamond 40÷60 μm. Wear resistance of Ni3Al–diamond sinters, tested by ball-on-disc method, showed that wear ratio is non-measurable and Ni3Al–diamond 40÷60 μm sinter has much lower friction factor than Ni3Al–diamond 16÷20 μm. Presented research has shown no influence of diamond particle size used in Ni3Al–diamond sinters on structural properties, however an increase of mechanical properties in composite with diamond 40÷60 μm can be noticed.

18

Charakterystyka kompozytów WCCo–cBN otrzymanych metodą PPS

Zieliński R., Wachowicz J., Michalski A., Oleszak D.

Inżynieria Materiałowa

|

2015

|

Vol. 36, nr 5

224--228

PL

Węglik wolframu w osnowie kobaltu jest jednym z najczęściej wykorzystywanych materiałów na narzędzia skrawające. W celu zwiększenia jego odporności na ścieranie wprowadza się rozproszone cząstki cBN, które mają kilkakrotnie większą odporność na ścieranie niż węgliki spiekane w osnowie kobaltu. W pracy przedstawiono wyniki badań otrzymywania kompozytu WC6Co–20% cBN metodą PPS (Pulse Plasma Sintering) na Wydziale Inżynierii Materiałowej Politechniki Warszawskiej. Spieki zostały wykonane w temperaturze 1050, 1100, 1200°C, były spiekane przez 300 s, ich gęstość wynosi odpowiednio 98,2%, 100% oraz 99,7% gęstości teoretycznej. Twardość spieku o 100% gęstości teoretycznej wynosi 2197 HV5. Dyfrakcja rentgenowska wykonana dla próbki spiekanej w temperaturze 1100°C przez 300 s nie ujawnia przejścia twardej odmiany cBN w niepożądaną i miękką strukturę hBN. Zdjęcia wykonane na skaningowym mikroskopie elektronowym w próbkach otrzymanych w temperaturze 1050°C ujawniają niepełne ukształtowanie ziarna węgliku wolframu, ponadto w strukturze obserwuje się występowanie porów. Obraz mikrostruktury próbki spiekanej w 1100°C przez 180 s przedstawia dobrze ukształtowane ziarno WC, występuje porowatość. Wydłużenie czasu spiekania do 300 s korzystnie wpływa na mikrostrukturę próbki, ziarno jest dobrze ukształtowane o charakterystycznych ostrych krawędziach, z dobrym umocowaniem ziaren cBN oraz brakiem zauważalnej porowatości. Zwiększenie temperatury spiekania do 1200°C sprzyja zjawisku powierzchniowej degradacji cząstek cBN (przemianie w niepożądaną strukturę hBN).

EN

One of the most widely used cutting tool materials is a tungsten carbide cobalt. Dispersed cBN particles are introduced in order to enhance abrasion resistance of this material and in the result it achieved several times greater wear resistance than cemented carbides in the matrix cobalt. In this paper the results of WC6Co–20% cBN composite, which are produced using PPS (Pulse Plasma Sintering) method at the Department of Materials Science and Engineering Warsaw University of Technology. The samples which were sintered at 1050, 1100, 1200°C during 300 s, their densities are 98.2%, 100% and 99.7% of the theoretical density. The hardness of the sinter of 100% (GT) is 2197 HV5. The X-ray diffraction carried out for a sample of 1100°C and sintering time was not revealed that passage of hard cBN in undesirable variations and soft structure hBN. The pictures, taken with an scanning electron microscope, of samples prepared at 1050°C discloses incomplete formation of tungsten carbide grain in addition to the structure observed in the presence of pores. Figure 9d of the microstructure of the sample which was sintered under temperature 1100°C during 180s shows a well-evolved is a porosity. With extending of a sintering time to 300 s the positive effect of the microstructure of sample was observed. A grain has well formation with sharp-edged with a good fastening of cBN grains moreover a lack of porosity was notice. Increasing of the sintering temperature to 1200°C is favorable for the phenomenon of surface degradation cBN particles (transformed to the undesired structure hBN).

19

Wpływ wstępnej selekcji informacji na jej dostępność

Michalski A.

Zeszyty Naukowe. Organizacja i Zarządzanie / Politechnika Śląska

|

2014

|

z. 68

345--354

PL

W początkowych rozdziałach artykułu zwrócono uwagę na znaczenie dostępności informacji w działalności biznesowej przedsiębiorstwa. Następnie omówiono przyczyny utraty dostępności informacji, szczególną uwagę zwracając na sprawę wstępnej selekcji. W dalszej części artykułu przedstawiono opis autorskiej adaptacji metodyki firmy Kepner-Tregoe (pierwotnie wykorzystywanej w działalności serwisowej) do wyjaśnienia przyczyn braku dostępności i przywracania dostępności informacji. Przedstawiono także rzeczywisty przykład, ilustrujący zastosowanie omówionej metodyki w praktyce.

EN

In the first chapters importance of information availability in the business activity of the enterprise is emphasized. Then the reasons of the information availability lost are discussed with preliminary selection as a special issue. In the next chapters description of the Kepner-Tregoe methodology author's adaptation for resolving problems with information unavailability is given. The procedure is illustrated with a real case study. In the paper there are three figures and eleven bibliographic entries.

20

Optymalizacja konstrukcji cewki przepływomierza elektromagnetycznego

Watral Z., Michalski A., Starzyński J.

Przegląd Elektrotechniczny

|

2014

|

R. 90, nr 8

236-238

PL

W artykule przedstawiono problematykę projektowania cewki wzbudzającej przepływomierza elektromagnetycznego dla kanałów otwartych i zamkniętych o przekroju prostokątnym. Porównano pod względem jakości generowanego pola magnetycznego cewkę typu double deck oraz cewkę Helmholtza. Zbadano wpływ długości cewki Helmholtza na rozkład pola magnetycznego w strefie pomiarowej kanału przepływowego.

EN

Paper presents some problems of excitation coil design for electromagnetic flow meter dedicated for open and close channels with rectangular cross section. Two types of coil were compared, double deck type and Helmholtz coil. The influence of the type and length of the Helmholtz coil on magnetic field distribution in measurement zone are discussed.