Effect of Nickel Equivalent on Structure and Corrosion Resistance of Nodular Cast Iron Ni-Mn-Cu

Medyński D., Janus A.

Archives of Foundry Engineering

|

2015

|

Vol. 15, iss. 1 spec.

69--74

EN

Within the research determined was the effect of nickel equivalent on structure, hardness and corrosion resistance of nodular cast iron Ni- Mn-Cu. The examinations revealed a drop of thermodynamic stability of austenite along with decreasing nickel content. Along with in-creasing degree of austenite transformation, the created martensite resulted in significant increase of hardness (and of abrasion resistance as well) of the examined of cast iron, accompanied by insignificant decrease of corrosion resistance.

2

Analysis of fracture mechanism in austenitic ductile iron with 30% Ni after impact test

Putyra P., Tabor A., Zarębski K.

Archives of Foundry Engineering

|

2008

|

Vol. 8, iss. 4

193-198

EN

The study presents the results of impact tests carried out on austenitic ductile iron with 30% Ni. The examined material was subjected to dynamic loads within a wide range of temperatures from (-196°C) to (+400°C). The fractures were examined under a JEOL JSM 6460LV scanning electron microscope. Additionally, microstructural examinations were carried out and chemical analysis in microregions was done by EDS.

3

Wpływ temperatury na właściwości mechaniczne sferoidalnego żeliwa austenitycznego o zawartości 20% niklu

Tabor A., Zarębski K., Putyra P.

Archiwum Odlewnictwa

|

2006

|

R. 6, nr 21/1

327-334

PL

W pracy przedstawiono wyniki statycznej próby rozciągania oraz z badań udarności austenitycznego żeliwa sferoidalnego o zawartoci 20% niklu. Właściwości mechaniczne obejmujące: wytrzymałość na rozciąganie, umowną granicę plastyczności, przewężenie, wydłużenie oraz udarność określono w szerokim zakresie temperatury od –196°C do 650°C. Dodatkowo zamieszczono fotografie struktury analizowanego materiału jak również fotografie przełomów ze statycznej próby rozciągania.

EN

This work presents results of the tensile properties of the austenitic nodular cast iron with 20% of nickel. The investigations were carried out in extensive range of temperature (from -196°C to 650°C) and lead to determination of: tensile strength; proof strength; elongation; reduction of area and impact strength for examined iron cast. Furthermore in this paper were placed photos of the microstructures of examined cast iron and photos of fracture surface of specimens after impact and tensile tests.

4

Wpływ niklu na właściwości wytrzymałościowe austenitycznego żeliwa sferoidalnego

Putyra P., Zarębski K., Tabor A.

Archiwum Odlewnictwa

|

2006

|

R. 6, nr 18/2

71--76

PL

W pracy przedstawiono wyniki badań właściwości mechanicznych dwóch rodzajów austenitycznego żeliwa sferoidalnego o różnej zawartości niklu (17% i 23%). Badania prowadzone w szerokim zakresie temperatury (od –196ºC do 650°C) miały na celu wyznaczenie dla analizowanych wytopów: wytrzymałości na rozciąganie (Rm), umownej granicy plastyczności (Rp0,2), wydłużenia (A5), przewężenia (Z) oraz udarności (KCV). W artykule zamieszczono również wyniki z pomiarów twardości (HRB) oraz zdjęcia mikrostruktur poszczególnych wytopów.

EN

This work presents results of the tensile properties of the austenitic nodular cast iron with different nickel content (17% i 23%). The investigation were carried out in extensive range of temperature (from-196°C to 650°C) and lead to determination of: tensile strength; proof strength; elongation; reduction of area and impact strength for examined iron cast. Furthermore in this paper were placed results from hardness mensuration and pictures presenting structure of each cast.