Wyniki wyszukiwania - BazTech

1

Effect of Surface Hydrophobization on the Durability of Concrete with Cement Kiln Dust

Grzegorczyk-Frańczak Małgorzata, Andrzejuk Wojciech, Hunek Robert, Łagód Grzegorz

Advances in Science and Technology. Research Journal

|

2024

|

Vol. 18, no 3

214--233

EN

The examinations of concrete involved partial substitution of cement with Cement Kiln Dust (CKD - 0, 5, 10, 20 and 30%). The water/cement (w/c) ratio amounted to 0.36. The obtained findings pertaining to open porosity, density, and volumetric density were found to correlate with the capillary action and absorptivity of the analyzed types of concrete. With the maximum addition of CKD, i.e. 30%, open porosity decreased by 35%. In turn, CKD added in the amount of 5% resulted in a slightly reduced addition compressive strength, amounting to 1.3% and 2.1% following 28 days and 56 days of concrete curing, respectively. After 28 days, the differences in strength were greater when the additive was supplied in higher amounts, i.e. 10%, 20%, and 30%, resulting in 6.5%, 13.4%, and 22.9% decrease, respectively, in spite of strength improvement. In terms of flexural and splitting tensile strengths, comparable relations were noted. As far as the frost resistance test results are concerned, the mass losses in all examined concretes were not significant, reaching up to 0.5%. The strength reduction in the case of the first three series of concretes was below 3%. When the CKD addition was increased to 20% and 30%, the value of the dynamic modulus of elasticity Ec,s decreased to a greater degree, by 8.0% and 14.7%, respectively. The hydrophobization effect is best seen in CKD-free concrete. After the impregnation, the loss of mass following the frost test of the samples is reduced by half. With a higher CKD content, the hydrophobization effectiveness is insignificant. The most favourable results were observed for hydrophobization with the oligomer-based preparation A1.

2

Hydrophobization of diatomaceous earth used to remove oil pollutants

Vogt Elżbieta, Topolska Karolina

Gospodarka Surowcami Mineralnymi

|

2023

|

T. 39, z. 2

209--222

EN

Contamination of the natural environment with petroleum pollution is still a frequent and particularly dangerous phenomenon, thus there is a need to remove these pollutants. Various types of mineral sorbents (silicate minerals, zeolites, perlite, diatomite, clay rocks) are highly valued in remediation processes due to their affordable, big selectivity and high efficiency. However, many sorbents are not resistant to moisture, which limits their use. The hydrophobization process improves the effectiveness of sorbents used in a humid environment. The DAMSORB produced by IM-POL was hydrophobized with a methanolic stearic acid solution. The use of cheap stearic acid as a modifier is economically advantageous. The evaluation of the hydrophobic properties of the modified material was performed on the basis of the results obtained from the tests: water absorption, floating on the water surface and the contact angles were determined. Tests of the sorption of petroleum-derived compounds were performed on the basis of three procedures: in accordance with the technical sheet of the leading producer of hydrophobic sorption materials in Poland, the Westighouse’s method in the oil layer and the Westighouse’s method on a flat surface. The modified sorbent floats on the surface of the water very well. The average value of the contact angle for the modified sample is 104 degrees. Material is super hydrophobic. In the water environment, the hydrophobized samples have a higher absorption capacity in relation to oil contaminations compared to the raw material. Features of the modified sorbent, such as good buoyancy on the water surface, low affinity to water and better absorption of oil from the solution, make it possible to use the material to remove petroleum contamination from water and highly moist surfaces.

PL

Skażenie środowiska naturalnego zanieczyszczeniami ropopochodnymi jest nadal częstym i szczególnie niebezpiecznym zjawiskiem, dlatego usuwanie tych zanieczyszczeń jest konieczne. Różnego rodzaju sorbenty mineralne (minerały krzemianowe, zeolity, perlit, ziemia okrzemkowa, skały ilaste) ze względu na przystępną cenę, dużą selektywność i wysoką wydajność są wysoko cenione w procesach remediacji. Jednak wiele z tych sorbentów nie jest odpornych na wilgoć, co ogranicza ich zastosowanie. Proces hydrofobizacji poprawia efektywność sorbentów stosowanych w wilgotnym środowisku. DAMSORB produkowany przez IM-POL zhydrofobizowano metanolowym roztworem kwasu stearynowego. Użycie taniego kwasu stearynowego jako modyfikatora jest korzystne ekonomicznie. Ocenę właściwości hydrofobowych modyfikowanego materiału przeprowadzono na podstawie wyników uzyskanych z badań: nasiąkliwości, unoszenia się na powierzchni wody oraz wyznaczono kąty zwilżania. Badania sorpcji związków ropopochodnych przeprowadzono w oparciu o trzy procedury: zgodnie z kartą techniczną wiodącego producenta hydrofobowych materiałów sorpcyjnych w Polsce, metodą Westighouse’a w warstwie olejowej oraz na powierzchni płaskiej. Modyfikowany sorbent bardzo dobrze unosi się na powierzchni wody. Średnia wartość kąta zwilżania dla zmodyfikowanej próbki wynosi 104 stopnie. Materiał jest superhydrofobowy. W środowisku wodnym próbki hydrofobizowane mają większą chłonność w stosunku do zanieczyszczeń olejowych w porównaniu z surowcem. Cechy modyfikowanego sorbentu, takie jak: dobra wyporność na powierzchni wody, niskie powinowactwo do wody oraz lepsza absorpcja oleju z roztworu pozwalają na zastosowanie materiału do usuwania zanieczyszczeń ropopochodnych z wody i powierzchni silnie zawilgoconych.

3

Modification of Concrete Surface with Higher Fatty Acids

Barnat-Hunek Danuta, Andrzejuk Wojciech, Szafraniec Małgorzata, Kachel Magdalena, Hunek Robert

Advances in Science and Technology. Research Journal

|

2023

|

Vol. 17, no 2

307--321

EN

The research presented in the paper concerns the production of innovative hydrophobizing agents and demonstration their effectiveness on a concrete surface. The starting materials are based on natural oils, water‒soluble silanes and siloxanes, and/or tap water. Aqueous preparations are characterized by properties which reduce the impact of volatile organic compounds (VOCs) on the environment, as they consist only of biodegradable components. Studies have shown that the higher fatty acids from vegetable oils and derived from the glycerin phase can be used as a component of concrete hydrophobizing agents, meeting the standard requirements for such agents. Analysis of the use of vegetable oil as a base compound for the production of industrial agents provides at least 95% confidence in its biodegradability. The reference concrete after the frost resistance test showed a weight loss of 1.8%. In the case of hydrophobization, the weight loss was 33.3 to 72% less than the reference samples. In the case of concrete hydrophobized with the glycerin agents, the salt crystallization occurred inside the structure of the material without causing any damage, with the reference concrete showing a weight loss of 0.8%.

4

Osuszanie zabytkowych murów fundamentowych metodą drenażu dwufunkcyjnego

Wójcik Robert

Materiały Budowlane

|

2022

|

nr 3

20--24

PL

Bardzo trudna jest ochrona zabytkowych budowli posadowionych na masywnych fundamentach przed wilgocią gruntową. Dotychczas stosowane metody są zawodne, a podejmowane działania niejednokrotnie przynoszą odwrotny efekt. Zachodzi zatem potrzeba poszukiwania nowych, bardziej skutecznych i mało inwazyjnych sposobów ochrony budowli przed wodą gruntową. W artykule przedstawiono wdrażaną obecnie autorską metodę drenażu dwufunkcyjnego, która polega na rozdzieleniu komina filtracyjnego na strefę osuszającą i odwadniającą. Umożliwiają to materiały najnowszej generacji, np. wodoszczelne i jednocześnie paroprzepuszczalne membrany separujące złoże osuszające.

EN

It is very difficult to protect historic buildings set on massive foundations against ground damp. The methods used so far are unreliable, and the taken actions often bring the opposite effects. Therefore, there is a need to search for new, more effective and minimally invasive methods of protecting structures against groundwater. The article presents the proprietary dual-purpose drainage method that is currently being implemented. The method consists on separating the filter zone (chimney) into a drying and drainage zone. It is possible thanks to the newest materials, such as waterproof and, at the same time, vapor-permeable membranes separating the drying bed.

5

Doświadczenia z produkcji prefabrykatów do budowy dużego obiektu sportowego

Kaprzyk Przemysław

Materiały Budowlane

|

2022

|

nr 5

38--39

6

Kryteria stosowania impregnacji hydrofobizującej mineralne materiały budowlane wg instrukcji WTA 3-17-10/D

Monczyński Bartłomiej

Izolacje

|

2021

|

R. 26, nr 11/12

88--96, 98

PL

Przedmiotem artykułu są kryteria stosowania impregnacji hydrofobizującej mineralne materiały budowlane wg instrukcji WTA 3-17-10/D. Autor omawia stan wiedzy na temat hydrofobizacji mineralnych materiałów budowlanych, nakreśla cel impregnacji hydrofobizującej, a następnie analizuje zasady stosowania środków hydrofobizujących, ryzyko stosowania środków hydrofobizujących, głębokość penetracji impregnatu, czynniki wywołujące zmiany na powierzchni materiału budowlanego, wpływ hydrofobizacji na procesy zachodzące w murze. Następnie przechodzi do zagadnień diagnostyki muru przed hydrofobizacją, przeciwwskazań do zabiegów hydrofobizacji oraz szacowania zużycia materiału hydrofobizującego oraz czasu impregnacji. Na koniec podaje charakterystykę i stosowanie różnych postaci preparatów hydrofobizujących oraz zasady bezpieczeństwa procesu impregnacji, z uwzględnieniem charakterystyki powierzchni próbnej impregnacji i nasiąkliwości kapilarnej. Na koniec zajmuje się problemami kontroli skuteczności impregnacji.

EN

The subject of the article is criteria for the use of impregnation for hydrophobization of mineral building materials according to the WTA 3-17-10/D instructions The author discusses the state of knowledge on the hydrophobization of mineral building materials, outlines the purpose of hydrophobing impregnation, and then analyses the principles of using hydrophobing agents, the risk of using hydrophobing agents, the penetration depth of the impregnate, factors causing changes on the surface of the building material, the effect of hydrophobization on the processes taking place in the wall. Then he goes to the issues of masonry diagnostics before hydrophobization, contraindications to hydrophobing treatment and estimating the consumption of hydrophobing material, as well as the impregnation time. Finally, he presents the characteristics and application of various forms of hydrophobing preparations as well as the safety rules of the impregnation process, taking into account the characteristics of the test surface of the impregnation and capillary absorption. Lastly, he deals with the problems of controlling the effectiveness of impregnation.

7

Magnetic field effects on surfactants adsorption on the solid surface as regards of its wettability

Hołysz Lucyna, Chibowski Emil, Terpiłowski Konrad

Physicochemical Problems of Mineral Processing

|

2020

|

Vol. 56, iss. 6

101--113

EN

The static magnetic field MF (0.44 T) effects on the adsorption of three surfactants: cationic bromide (DTAB) and hexadecyltrimethylammonium bromide (CTAB), and anionic sodium dodecylsulfate (SDS) from their 10-3 M solutions were studied on bare and low-temperature air plasma treated glass plates. The surface properties of the adsorbed surfactants layers were determined via the water advancing and receding contact angles measurements and then calculation of the apparent surface free energy. An optical profilometer was used to determine the structure and topography of the adsorbed layers. The DTAB and SDS concentrations were below their critical micelle concentration and that of CTAB very close to its cmc. The results showed that in the case of DTAB solution (much below its cmc) a small decrease in the contact angle appeared while in CTAB (close to its cmc) an increase in the contact angle value was observed if adsorbed in the MF presence. Quite good reproducibility of the contact angle values was obtained. This was not the case for the SDS solution where the contact angle values were scattered. The reason was that the anionic surfactant did not adsorb homogeneously on the negatively charged glass surface. The contact angles and the calculated values of the work of water spreading clearly show that MF influences the structure of the surfactant adsorbed layer which was also supported by the optical profilometry images.

8

Fabrication of transparent polysiloxane coatings on a glass support via the sol-gel dip coating technique and the effect of their hydrophobization with hexamethyldisilazane

Chodkowski Michał, Terpiłowski Konrad, Pasieczna-Patkowska Sylwia

Physicochemical Problems of Mineral Processing

|

2020

|

Vol. 56, iss. 6

76--88

EN

This study aimed at synthesis, preparation, and physicochemical properties investigation of undoped polysiloxane-based coatings deposited on the glass supports. The other goal was to test the effectiveness of their hydrophobization with hexamethyldisilazane at an elevated temperature using a bubbler. The coatings were obtained in a sol-gel process by acid-assisted hydrolysis of tetraethoxysilane and they were applied to the glass supports using the dip coating technique with various withdrawal speeds. The synthesized composition was scanned using TurbiscanLAB and its particle size was determined by means of the dynamic light scattering technique. The obtained surfaces were examined based on the water wettability measurements, photoacoustic spectroscopy, and transmittance measurements. It was found that the stability of the sol did not change during the dip-coating. Smooth, homogeneous, uniform, hydrophobic, and transparent coatings on the glass supports were obtained. Their wettability was determined by the contact angle in the range from 83.5 to 95.2 degrees and very low contact angle hysteresis. The hydrophobic effect obtained by modification with hexamethyldisilazane appears to be permanent – the contact angles do not change significantly after 7 days. The synthesized sol composition appears to be a good starting point for its chemical and physical modification for hydrophobicity increase and surface properties modification. Moreover, the hydrophobization of the coatings with hexamethyldisilazane at an elevated temperature using the bubbler did not have the desired effect.

9

Zapobieganie degradacji murów licowych

Wesołowska Maria

Materiały Budowlane

|

2020

|

nr 12

44--46

10

Modification of activated carbons for application in adsorption cooling systems

Wolak Eliza, Vogt Elżbieta, Szczurowski Jakub

Technical Sciences / University of Warmia and Mazury in Olsztyn

|

2019

|

nr 22(1)

87--98

EN

In this paper commercially available activated WD-extra carbon (Gryfskand) which is applied for water treatment was used. Activated carbon was modified by the following chemical agents: H2O2, HNO3 and HCl. Chemical modifications significantly affect the chemical, structural and surface properties of activated carbons. Hydrophobization with ethereal stearic acid was performed on the raw material and samples after chemical modification. Hydrophobic properties of the samples were specified. The relationship of the chemical modification agents with hydrophobization degree was indicated. The thermal effects of wetting by methanol was measured. The heat of wetting was calculated. The purpose of the work was to modify the WD carbon properties to obtain an adsorbent for cooling systems characterized by both good thermal capacity and moisture resistance. The modifying chemical substances applied accounted for an increase in the concentration of the acid functional groups. The hydrophobized and HCl-modified WD(HCl) carbon has the best hydrophobized properties. The results of studies describing such modifications allow to conclude that the use of hydrophobic materials may lead to the production of sorbents with new functions facilitating their storage and use.

11

Przejawy korozji biologicznej kamienia budowlanego i problemy związane z jego rewaloryzacją

Rembiś Marek

Przegląd Geologiczny

|

2019

|

Vol. 67, nr 9

710--716

EN

Biological corrosion (biodeterioration) of a building material resulting from the presence of micro- and macroorganisms that occupy the stone impairs its properties and may even lead to its full damage (disintegration). The stone conservation procedures usually start with surface disinfection and are followed by consolidation (stone structure strengthening) and surface hydrophobization (inducing water repellency). Thus, the stone is penetrated almost simultaneously by a range of various chemicals. The combined interaction of the substances of various chemistry may lower their effectiveness and even result in a failure to obtain the desired stone restoration. Author’s SEM observations have proved that some of the biocidal substances hamper a later introduction ofchemicals, which eitherform appropriate films consolidating the sandstone structure or make the stone hydrophobic. Such adverse effects of the multichemical stone treatment have also been evidenced by the measurements of the sandstone compression strength and water absorbability

12

Hermon – środek do odgrzybiania i hydrofobizacji murów. Istota działania i doświadczenia praktyczne

Kłosiński Bogdan Stanisław

Przegląd Budowlany

|

2019

|

R. 90, nr 11

34--39

PL

W artykule wskazano środek Hermon jako produkt prac naukowo-badawczych przedsiębiorstwa OKTIMA Sp. z o.o. w Bydgoszczy i efekty jego stosowania. Technologia zabezpieczeń murów przed działaniem czynników wilgotnościowych jest objęta patentem, działającym na terenie Rzeczypospolitej Polskiej: Patent nr 192514 na wynalazek pt. Środek do odgrzybiania i hydrofobizacji murów. Środek ten znalazł zastosowanie w szeregu przypadków zabezpieczania murów przed wilgocią, w szczególności podnoszoną kapilarnie wskutek nieskutecznych zabezpieczeń izolacją poziomą (lub jej brakiem). Pokazane zastosowanie tego środka ukazuje jego skuteczność mimo braku fizycznej ingerencji w głąb muru.

EN

The article indicates the Hermon measure as a product of research and development of OKTIMA Sp. z o.o. in Bydgoszcz and the effects of its use. The technology of wall protection against the effects of humidity factors is covered by a patent operating in the Republic of Poland: Patent No. 192514 for the invention entitled A remedy for mucilage and hydrophobization of walls. This measure has been used in a number of cases of wall protection against moisture, in particular capillary rising due to ineffective protection against horizontal (or lack of) insulation. The shown applications of this remedy show its effectiveness despite the lack of physical interference into the wall.

13

Wytwarzanie powłok z użyciem organofunkcyjnych silanów

Martyła A., Osińska-Broniarz M., Kopczyk M., Sztorch B., Jarmołowicz A., Przekop R. E.

Przemysł Chemiczny

|

2017

|

T. 96, nr 6

1244--1248

PL

Zaprezentowano wyniki badań mających na celu ocenę powłok otrzymywanych z użyciem preparatów do hydrofobizacji. Podłożem bazowym, poddawanym modyfikacji był piaskowiec, granit oraz podłoże szklane. Badaniom poddano preparaty dostępne komercyjnie oraz ich modyfikacje dokonane z wykorzystaniem oleju silikonowego i organofunkcyjnego silanu. Ocenę właściwości hydrofobowych wykonano poprzez pomiar kątów zwilżania modyfikowanych materiałów.

EN

B-Si glass, sandstone and granite surface were modified by coating with com. hydrophobic formulations and their mixts. with silicone oil and organofunctional silanes and studied by measuring their wetting angles. A substantial increase in the sandstone and granite hydrophobicity was achieved. The glass surface showed low hydrophobizability.

14

Zabezpieczanie żelbetowych obiektów inżynierskich metodą hydrofobizacji

Błaszczyński T. Z., Osesek M., Gwozdowski B., Ilski M.

Materiały Budowlane

|

2017

|

nr 4

52--54

PL

Beton jest niezmiennie jednym z najczęściej stosowanych materiałów konstrukcyjnych, również w przypadku konstrukcji mostów, estakad czy wiaduktów. Wraz z upływem lat, niezwykle ważnym problemem staje się degradacja betonu, która może przyspieszać korozję stali zbrojeniowej i drastycznie obniżać nośność konstrukcji. W artykule przeanalizowano możliwość wykorzystania hydrofobizacji wgłębnej do naprawy żelbetowych obiektów inżynierskich. Przedstawiono korzyści wynikające z właściwego zabezpieczenia konstrukcji żelbetowych przed niszczącym oddziaływaniem promieniowania UV, szkodliwych gazów czy postępującą korozją chlorkową, zwłaszcza w przypadku budowli mostowych. Wskazano również na potrzebę kalkulacji kosztów realizacji inwestycji wraz z przewidywanymi kosztami utrzymania obiektu oraz duży udział kosztów obsługi logistycznej w całkowitych kosztach prac naprawczych.

EN

Concrete is, unchangeably, one of the most frequently applied building materials, also in the case of bridges, overpasses or viaducts. Along with the aging of such structures, the degradation of concrete, which may accelerate the corrosion of reinforcing steel and drastically decrease the load-bearing capacity of the structure, becomes an important issue. The paper analyzes the possibilities of using deep hydrophobisation in repairing reinforced concrete engineering structures. The benefits of properly securing reinforced concrete structures from the damaging effects of UV radiation, the influence of harmful gases, or progression of chlorine induced corrosion have been presented, especially in regards to bridge structures. The need to calculate the costs of carrying out investments along with the expected costs of maintaining such structures, as well as the high share of costs connected with logistics, has also been indicated in the total costs of repair works.

15

Hydrofobizacja strukturalna metodą iniekcji materiałów drobnoporowatych

Trochonowicz M.

Izolacje

|

2017

|

R. 22, nr 6

68--73

PL

W artykule zaprezentowano wyniki badań dotyczących możliwości hydrofobizacji skał wapiennych metodą iniekcji. Omówiono zagadnienia dotyczące hydrofobizacji jednej ze skał wapiennych – opoki wapnistej.

EN

The article presents the results of studies of water repellent capacity of limestones applied through injection. The aspects of hydrophobization are discussed for one type of limestone, namely calcareous bedrock.

16

Estryfikacja skrobi ziemniaczanej kwasem oleinowym w obecności lipazy z Candida antarctica w polu mikrofalowym oraz w warunkach ogrzewania konwencjonalnego

Ptak S., Żarski A., Antczak T., Kapuśniak J.

Polimery

|

2016

|

T. 61, nr 6

442--448

PL

Estryfikowano natywną skrobię ziemniaczaną długołańcuchowym nienasyconym kwasem oleinowym w obecności lipazy pochodzącej z Candida antarctica, immobilizowanej na nośniku polimerowym. Reakcję prowadzono w polu mikrofalowym oraz w warunkach ogrzewania konwencjonalnego. Przebieg estryfikacji potwierdzono za pomocą spektroskopii w podczerwieni FT-IR i magnetycznego rezonansu jądrowego 1H NMR, proszkowej dyfrakcji rentgenowskiej (XRD) oraz skaningowej mikroskopii elektronowej (SEM). Stwierdzono, że otrzymany produkt termoplastyczny wykazuje większą hydrofobowość niż natywna skrobia ziemniaczana.

EN

An attempt has been made to prepare hydrophobic, thermoplastic material through esterification of potato starch with long-chain unsaturated fatty acid. The esterification was conducted in the presence of fungal lipase from Candida antarctica immobilized on apolymer carrier. Reaction was conducted in amicrowave field and, for comparison, under conventional heating. The completion of the esterification reaction was confirmed by spectroscopic FT-IR and 1H NMR methods, X-ray powder diffraction and scanning electron microscopy (SEM). It was found that the obtained product exhibited higher hydrophobicity than native potato starch.

17

Hydrofobizowane tynki z zeolitem

Barnat-Hunek D., Klimek B.

Materiały Budowlane

|

2016

|

nr 9

14--16

PL

Artykuł poświęcony jest ocenie skuteczności hydrofobizacji tynków z zeolitem. Hydrofobizację w masie uzyskano, stosując domieszki hydrofobowe. Hydrofobizację powierzchniową wykonano przy użyciu wodnej emulsji żywicy metylosilikonowej w wodorotlenku potasu i alkiloalkoksysilanu w rozpuszczalniku organicznym. Przeprowadzono badania podstawowych parametrów mechanicznych i fizycznych. Wszystkie próbki użyte w badaniach wykazały dobrą odporność na krystalizację soli po 15 cyklach. Hydrofobizacja przy użyciu mineralnej zaprawy uszczelniającej (Z2) nie chroni w wystarczającym stopniu zaprawy z zeolitem przed korozją mrozową, a hydrofobizacja powierzchniowa w znacznym stopniu wpłynęła na mrozoodporność tynków.

EN

The article is devoted to assessing the effectiveness of hydrophobisation of plasters with zeolite. Hydrophobisation of the mass was performed using a hydrophobic admixture and surface hydrophobisation was produced using: a water-based emulsion of methyl silicone resin in potassium hydroxide and alkyl-alkoxy-silane in organic solvents. Measurements of the basic mechanical and physical parameters were carried out. All the samples used in the research demonstrated good resistance to salt crystallization after 15 cycles. Hydrophobisation by the use of mineral waterproofing grout (Z2) does not protect to a sufficient degree mortar with zeolite against corrosion frost. Surface hydrophobisation had a considerable impact on the frost-resistant properties of the plasters.

18

Ceramika vs. woda

Miechowicz D.

Ceramika Budowlana

|

2016

|

nr 1-2

23--24

PL

W ostatnich latach zwiększa się zainteresowanie zagadnieniem hydrofobizacji materiałów budowlanych, w tym szczególnie kamienia naturalnego i ceramiki. O co chodzi w tym mądrze brzmiącym terminie? W skrócie - o to, by powierzchnia cegieł czy dachówek nie chłonęła wody, a jednocześnie odznaczała się zdolnością odparowywania wilgoci, która już znajduje się w materiale.

19

Ocena stanu technicznego komina murowanego i badania eksperymentalne cegły

Barnat-Hunek D., Smarzewski P., Szafraniec M.

Wiadomości Konserwatorskie

|

2015

|

Nr 41

7--19

PL

W artykule przedstawiono ocenę stanu technicznego komina murowanego z cegły oraz zaproponowano zakres prac remontowych. Badania skuteczności hydrofobizacji komina poprzedziła dokładna diagnostyka obiektu, która polegała na sprawdzeniu m.in. zawartości soli i stopnia zawilgocenia płaszcza komina, ponieważ wysoki stopień zasolenia i duża zawartość wody w porach materiału wyklucza zastosowanie hydrofobizacji. Materiał badawczy stanowiła cegła pobrana z płaszcza przemysłowego komina murowanego. W części eksperymentalnej dokonano obiektywnej oceny preparatów, które mogą być wykorzystane do hydrofobizacji powierzchni komina.

EN

The aim of the research presented in the paper was to evaluate the technical condition of the masonry chimney and to propose scope of modernization process. The studies of effectiveness of hydrophobization were preceded by a thorough diagnosis of the building, which involved checking of the salt content and the degree of moisture of chimney jacket. If the salt content and water content in the pores of the material were too high the hydrophobization could not be used. In presented paper the brick from industrial jacket of chimney was tested. Experimental section contains an objective evaluation of preparations which can be used for the chimney surface hydrophobization.

20

Właściwości adhezyjne małocząsteczkowego polimeru modyfikowanego nanokrzemionką i dezintegrowanego ultradźwiękami przeznaczonego do hydrofobizacji ceramiki budowlanej

Fic S., Kłonica M., Szewczak A.

Polimery

|

2015

|

T. 60, nr 11-12

730--734

PL

Zbadano skuteczność hydrofobizacji powierzchni cegły ceramicznej pełnej za pomocą preparatu na bazie nanopolimerów. Proces polegał na zanurzeniu cegły na 15 s w roztworze nanopolimeru modyfikowanego dodatkiem nanokrzemionki i dezintegrowanego ultradźwiękami. Miarą właściwości adhezyjnych hydrofobowej nanobłonki powstałej na powierzchniach cegieł była wartość swobodnej energii powierzchniowej γs (SEP) wyznaczanej metodą Owensa—Wendta na podstawie kątów zwilżania powierzchni próbek wodą destylowaną oraz dijodometanem. Oceniano wpływ ultradźwięków oraz dodatku nanokrzemionki do roztworu polimeru na wybrane właściwości adhezyjne hydrofobizowanej powierzchni badanego materiału.

EN

The results of studies on the effectiveness of hydrophobization of ceramic brick surface using a formulation based on nanopolymers are described. Each series of the specimenswas immersed for 15 s in a solution of nanopolymer — whose structure and composition were additionally modified with nanosilica — and subjected to ultrasonication. The adhesive properties of the hydrophobic nanofilm created on the surface of the bricks were determined by measuring the surface free energy γs (SFE) with Owens—Wendt method using the contact angles of the specimen surface for distilled water (strongly polar liquid) and diiodomethane (non-polar liquid). Based on these results, the effects of sonication and addition of nanosilica on the selected adhesive properties of the material surface were investigated.