Microstructure and Oxidation Resistance of Laser Remelted Plasma Sprayed Nicraly Coating

Autorzy Niemiec, D.  Moskal, G.  Carski, Ł. 
Treść / Zawartość
Warianty tytułu
Języki publikacji EN
Abstrakty
EN The article presents results of research relating to the impact of laser treatment done to the surface of plasma sprayed coatings NiCrAlY. Analysis consisted microstructure and oxidation resistance of coatings subjected to two different laser melting surfaces. The test were performed at a temperature 1000°C the samples were removed from the furnace after 25, 300, 500, 750 and 1000 hours. The investigations range included analysis of top surface of coatings by XRD characterization oxides formed types and microscopic investigations of coatings morphology
Słowa kluczowe
EN NiCrAlY coatings   laser remelted   oxidation resistance  
Wydawca Polish Academy of Sciences, Committee of Metallurgy, Institute of Metallurgy and Materials Science
Czasopismo Archives of Metallurgy and Materials
Rocznik 2016
Tom Vol. 61, iss. 2B
Strony 1183--1191
Opis fizyczny Bibliogr. 13 poz., rys., tab., wykr.
Twórcy
autor Niemiec, D.
autor Moskal, G.
  • Silesian University of Technology, 8 Krasińskiego Str., 40-019 Katowice, Polska
autor Carski, Ł.
  • Silesian University of Technology, 8 Krasińskiego Str., 40-019 Katowice, Polska
Bibliografia
[1] J. Quadakkers, A. K. Tyagi, D. Clemens, R. Anton, L. Singheiser, The significance of bond coat oxidation for the life of TBC co atings, Elevated temperature coatings: surface and technology III, The minerals, Metals & Materials Society, 119-130, (1999).
[2] L. Swadźba, G. Moskal, B. Mendala, M. Hetmańczyk, Characterization of microstructure and properties of TBC systems with gradient of chemical composition and porosity, Archives of Metallurgy and Materials 53(3), 945-954, (2008).
[3] M. Zielińska, J. Sieniawski, M. Zagula-Yavorska, M. Motyka, Influence of chemical composition of nickel based superalloy on the formation of aluminide coatings, Archives of Metallurgy and Materials 1, 193-197, (2011).
[4] M. Zagula-Yavorska, J. Sieniawski, M. Zielińska, Functional properties aluminide layer deposited by CVD method on Inconel 713 LC Ni-base superalloy, Archives of Metallurgy and Materials 1, 187-192, (2011).
[5] G. Moskal, M. Góral, L. Swadźba, B. Mendala, M. Hetmańczyk, B. Witala, Microstructural characterization of gas phase aluminized TiAlCrNb intermetallic alloy, Archives of Metallurgy and Materials 57, 253-259, (2012).
[6] G. Moskal, L. Swadźba, B. Mendala, M. Góral, M. Hetmańczyk, Degradation of the TBC system during the static oxidation test, Journal of Microscopy 237(3), 450-455 (2010).
[7] H. E. Evans, A. Stawbridge, R. A. Carolan, C. B. Ponton, Creek effects on the spallation of alumina layer from a NiCrAlY coating 225, 1-8 (1997).
[8] A. G. Evans, G. B. Crumly, R. E. Demaray, The mechanical behavior of brittle coatings and layers, Oxidation of Metals 20, 193-216 (1983).
[9] D. Naumenko, V. Shermet, L. Singheiser, W. J. Quadakkers,Failure mechanism of thermal barrier coatings on MCrAlY-type bondcoats associated with the formation of the thermally grown oxide, Journal of Materialas Science 44, 1687-1703 (2009).
[10] C. H. Hsueh, et al., Effects of interface roughess on residual stresses in thermal barrier coatings, Journal of American Ceramic Society 82, 1073-1075 (1999).
[11] F. Tang, J. Schoenung, Local accumulation of thermally grown oxide in plasma-sprayed thermal barrier coatings with rough top- -coat/bond-coat interfaces, Scripta Materiallia 52, 905-909 (2005).
[12] G. Moskal, Degradation process of NiCrAlY coatings during oxidation, Ochrona przed Korozją 55, 189-192 (2012).
[13] D. Niemiec, G. Moskal, M. Mikuśkiewicz, A. Mościcki, P. Kałamarz, Ł. Carski, Influence of top-surface conditio on oxidation resisatnce of NiCrAlY coating on Inconel 625, Ochrona przed korozją 7, 255-261 (2014).
Uwagi
EN We gratefully acknowledge the financial support of the Structural Funds in the Operational Program. Innovative Economy (TEOP) finance by the European Regional Development Fund, Project No. POIG. 01.01.02-00-015/09.
PL Opracowanie ze środków MNiSW w ramach umowy 812/P-DUN/2016 na działalność upowszechniającą naukę
Kolekcja BazTech
Identyfikator YADDA bwmeta1.element.baztech-fe9484c4-6220-465f-8c08-3dd7e5003360
Identyfikatory
DOI 10.1515/amm-2016-0197