Effect of the Drawing Speed on the Delaminations in the Torsion Test of High-Carbon Steel Wires

Autorzy
Treść / Zawartość
Identyfikatory
Warianty tytułu
Języki publikacji
EN
Abstrakty
EN
In this paper, an attempt was made to explain the causes of surface delamination in high carbon steel wires during the torsion test. For end wires with 1.7 mm diameter drawn at speeds of 5, 10, 15, 20, 25 m/s, technological tests were carried out. Then the susceptibility of the wire to plastic strain was determined. The microstructure analysis complemented the research. Analysis of the fracture torsion test showed that the wires drawn at speeds exceeding 15 m/s are delamination, which disqualify it as a material for a rope and a spring. The source of delamination in high carbon steel wires is their stronger strengthening, especially of the surface layer, which leads to a decrease in the orientation of the cementite laminaes and an increase in the degree of their fragmentation.
Słowa kluczowe
Rocznik
Strony
671--675
Opis fizyczny
Bibliogr. 17 poz., fot., rys., tab.
Twórcy
autor
  • Czestochowa University of Technology, Faculty of Production Engineering and Materials Technology, Institute of Metallurgy and Metals Technology, 19 Armii Krajowej Str., 42-201 Częstochowa, Poland, suliga@wip.pcz.pl
Bibliografia
  • [1] M. Suliga, Analysis of the heating of steel wires during high speed multipass drawing process. Archives of Metallurgy and Materials 59 (4), 1475-1480 (2014).
  • [2] H. Delrue, J. Van Humbeck, E. Aernoudt, I. Lefever, W. Van Raemndock, A study of aging of hard drawn pearlitic steel wire by Differential Scanning Calorimetry (DSC) and Thermoelectric Powder (TEP), Wire Journal, April, 74-79 (1997).
  • [3] P. Watte, J. Van Humbeck, E. Aernoudt, I. Lefever, Strain ageing in heavily drawn eutectoid steel wire. Scripta Materialia 34, 1, 89-95 (1996).
  • [4] E. Aernoudt, Materials response to wire drawing. Wire Journal International, March, 53-63 (1983).
  • [5] Roger N. Wright, Physical conditions in the lubricant layer.Wire Journal International, August, 88-92 (1997).
  • [6] J. Nemec, Rigidity and Strength of Steel Parts. Academia Publishing House of Czechoslovak Academy of Sciences, Prague (1966).
  • [7] J. G. Sevillano, Room temperature plastic deformation of pearlite cementite. Materials Sience and Eengineering 21, 221-230 (1975).
  • [8] L. Godecki, Analiza przyczyn powstawania rozwarstwień powierzchniowych drutów sprężynowych ze stali wysokowęglowych podczas próby skręcania, Praca habilitacyjna, ZN Politechniki Śląskiej, Gliwice (1972).
  • [9] J. W. Pilarczyk, Analiza przyczyn zmian własności drutów ciągnionych konwencjonalnie i w ciągadłach ciśnieniowych. Seria monografie nr 39, Wydawnictwo Politechniki Częstochowskiej, Częstochowa (1996).
  • [10] W. V. Raemdanck, I. Lefever, U. D’Haene, Torsion tests as a tool for high strength wire evaluation, Wire Journal International, June, 68-75 (1994).
  • [11] J. G. Sevillano, A twist on heavily drawn wires. Mordica Memorial Lecture, WAI’s 80th Annual Convention, 12 May (2010).
  • [12] E.A.D. Aernoudt, Drawing induced structural and mechanical anisotropy. Mordica Memorial Lecture, WAI’s 79th Annual Convention, 27 April (2009).
  • [13] M. Zelin, Microstructure evolution in pearlitic steels during wire drawing. Acta Materialia 50, 4431-4447 (2002).
  • [14] Durgaprasad A., Giri S., Lenka S., Sarkar S. K., Biswas A., Kundu S., Mishra S., Chandra S., Doherty R. D., Samajdar I., Delamination of Pearlitic Steel Wires: The Defining Role of Prior-Drawing Microstructure, Metallurgical and Materials Transactions A 49, 6, 2037-2047 (2018).
  • [15] Yamasaki S., The microstructure and mechanical properties of drawn and aged pearlitic steel wires, Materials Science and Technology 34, 2, 0267-0836 (2018).
  • [16] Tanaka M., Manabe T., Morikawa T., Higashida, K., Mechanism Behind the Onset of Delamination in Wire-drawn Pearlitic Steels, Tetsu-to-Hagane 105, 2, 155-162 (2019).
  • [17] F. Knap, R. Karuzel, Ł. Cieślak, Ciągnienie drutów, prętów i rur, Metalurgia Nr 36, Wydawnictwo Wydziału Inżynierii Procesowej, Materiałowej i Fizyki Stosowanej, Politechniki Częstochowskiej, Częstochowa (2004).
Uwagi
PL
Opracowanie rekordu w ramach umowy 509/P-DUN/2018 ze środków MNiSW przeznaczonych na działalność upowszechniającą naukę (2019).
Typ dokumentu
Bibliografia
Identyfikator YADDA
bwmeta1.element.baztech-e6c30dae-09f5-4034-82c6-52ad6d2963ea
JavaScript jest wyłączony w Twojej przeglądarce internetowej. Włącz go, a następnie odśwież stronę, aby móc w pełni z niej korzystać.