Thermovisual analysis of stainless steel sheet heating

Wybrane pełne teksty z tego czasopisma
Identyfikatory
Warianty tytułu
PL
Analiza termowizyjna podgrzewania blachy stalowej nierdzewnej
Języki publikacji
EN
Abstrakty
EN
The purpose of warm forming is to reduce the deformation resistance, and therefore the formation of products at reduced pressures. A key problem associated with warm sheet metal forming is uniform heating of the material to a required temperature. This task is carried out mostly by using resistance heating plates. The article presents the results of the analysis of the thermal state of a heating plate for induction heating of an AMS 5604 stainless steel sheet. To determine the temperature distribution on the sheet surface an FLIR P 640 thermal imaging camera was used. It was found that the temperature difference on the outer surface of sheets preheated to the temperature of 900°C was about 300°C. A large difference in the temperature on the outer surface of the sheet means that the analysed device cannot be successfully used in the heating process of stainless steel sheets. After the application of a layer of graphite on the sheet surface to increase the emissivity, areas of low emissivity as a result of graphite detachment from the sheet surface were observed.
PL
Celem obróbki plastycznej na półgorąco jest obniżenie oporu plastycznego, a zatem kształtowanie wyrobów przy obniżonych naciskach. Kluczowym problemem związanym z kształtowaniem blach na półgorąco jest równomierne podgrzanie materiału do wymaganej temperatury. Zadanie to jest realizowane najczęściej za pomocą oporowych płyt grzewczych. W pracy przedstawiono wyniki analizy stanu termicznego płyty grzejnej do indukcyjnego podgrzewania blach ze stali nierdzewnej AMS 5604. Do określenia rozkładu temperatury na powierzchni blachy wykorzystano kamerę termowizyjną FLIR P 640. Stwierdzono, że gradient temperatury w materiale podgrzewanym do temperatury 900°C wynosi około 300°C. Tak duża różnica w temperaturze na powierzchni płyty powoduje, że analizowane urządzenie nie może być z powodzeniem wykorzystane w procesie podgrzewania blach stalowych nierdzewnych. Po naniesieniu na powierzchnię blachy warstwy grafitu w celu zwiększenia emisyjności zaobserwowano obszary o niskiej emisyjności powstałe w wyniku odklejenia grafitu od powierzchni blachy.
Rocznik
Strony
377--384
Opis fizyczny
Bibliogr. 24 poz., rys., wykr.
Twórcy
  • Rzeszow University of Technology, 12 Powstańców Warszawy Ave., 35-959 Rzeszów
  • Rzeszow University of Technology
  • Rzeszow University of Technology
  • Pratt & Whitney Rzeszów
autor
  • Pratt & Whitney Rzeszów
Bibliografia
  • [1] Stachowicz F., Trzepieciński T., Pieja T.: Warm forming of stainless steel sheet, Arch. Civ. Mech. Eng., 10 (2010) 85-94.
  • [2] Takuda H., Mori K., Masachika T., Yamazaki E., Watanabe Y.: Finite element analysis of the formability of an austenitic stainless steel sheet in warm deep drawing, J. Mater. Proc. Tech., 143-144 (2003) 242-248.
  • [3] Lonardelli I., Bosetti P., Bruschi S., Molinari A.: On the formability and microstructural characteristics of AISI 301 parts formed by single-point incremental forming, Key Eng. Mater., 473 (2011) 869-874.
  • [4] Iguchi T., Ujiro T.: Effect of imposing temperature gradient in stretch forming process for ferritic stainless steel sheets, AIP Conf. Proc., 1252 (2010) 1193-1200.
  • [5] Shankar V., Bhanu Sankara Rao K., Mannan S.L.: Microstructure and mechanical properties of Inconel 625 superalloy, J. Nucl. Mater., 288 (2001) 222-232.
  • [6] Shankar V., Valsan M., Bhanu Sankara Rao K., Mannan S.L.: Room temperature tensile behavior of service exposed and thermally aged alloy 625, Scripta Mater., 44 (2001) 2703-2711.
  • [7] Yi S., Bohlen J., Heinemann F., Letzig D.: Mechanical anisotropy and deep drawing behaviour of AZ31 and ZE10 magnesium alloy sheets, Acta Mater., 58 (2010) 592-605.
  • [8] Mekonen M.N., Steglich D., Bohlen J., Letzig D., Mosler J.: Mechanical characterization and constitutive modeling of Mg alloy sheets, Mat. Sci. Eng. A-Struct., 540 (2012) 174-86.
  • [9] Palumbo G., Sorgente D., Tricarico L., Zhang S.H., Zheng W.T.: Numerical and experimental investigations on the effect of the heating strategy and the punch speed on the warm deep drawing of magnesium alloy AZ31, J. Mater. Proc. Tech., 191 (2007) 342-346.
  • [10] Ren L.M., Zhang S.H., Palumbo G., Sorgente D., Tricarico L.: Numerical simulation on warm deep drawing of magnesium alloy AZ31 sheets, Mat. Sci. Eng. AStruct., 499 (2009) 40-44.
  • [11] Lee Y.S., Kwon Y.N., Kang S.H., Kim S.W., Lee J.H.: Forming limit of AZ31 alloy sheet and strain rate on warm sheet metal forming, J. Mater. Proc. Tech., 201 (2008) 431-435.
  • [12] Zhang S.H., Zhang K., Xu Y.C., Wang Z.T., Xu Y., Wang Z.G.: Deep-drawing of magnesium alloy sheets at warm temperatures, J. Mater. Proc. Tech., 185 (2007) 147-151.
  • [13] Chang Q.F., Li D.Y., Peng Y.H., Zeng X.Q.: Experimental and numerical study of warm deep drawing of AZ31 magnesium alloy sheet, Int. J. Mach. Tool. Manuf., 47 (2007) 436-43.
  • [14] Lee Y.S., Kim M.C., Kim S.W., Kwon Y.N., Choi S.W., Lee J.H.: Experimental and analytical studies for forming limit of AZ31 alloy on warm sheet metal forming, J. Mater. Proc. Tech., 187-188 (2007) 103-107.
  • [15] Kurukuri S., van den Boogaard A.H., Miroux A., Holmedal B.: Warm forming simulation of Al-Mg sheet. J. Mater. Proc. Tech., 209 (2009) 5636-5645.
  • [16] Wang W., Huang L., Tao K., Chen ., Wei X.: Formability and numerical simulation of AZ31b magnesium alloy sheet in warm stamping process, Mater. Des., 87 (2015) 835-844.
  • [17] Bagheriasl R., Worswick M., McKinley J., Simha H.: An effective warm forming process; numerical and experimental study, Int. J. Mater. Form., 3 (2010) 219-222.
  • [18] Laurent H., Coer J., Manach P.Y., Oliveira M.C., Menezes L.F.: Experimental and numerical studies on the warm deep drawing of an Al-Mg alloy, Int. J. Mech. Sci., 93 (2015) 59-72.
  • [19] Zhang K.F., Yin D.L., Wu D.Z.: Formability of AZ31 magnesium alloy sheets at warm working conditions, Int. J. Mach. Tool. Manu., 46 (2006) 1276-1280.
  • [20] Takuda H., Mori K., Masuda I., Abe Y., Matsuo M.: Finite element simulation of warm deep drawing of aluminium alloy sheet when accounting for heat conduction, J. Mater. Proc. Tech., 120 (2002) 412-418.
  • [21] Li D., Ghosh A.K.: Biaxial warm forming behavior of aluminum sheet alloys, J. Mater. Proc. Tech., 145 (2004) 281-293.
  • [22] Lee M.H., Kim H.Y., Kim H.J., Choi Y.C., Oh S.I.: Numerical modeling of magnesium alloy sheet metal forming at elevated temperature, AIP Conf. Proc., 908 (2007) 569-574.
  • [23] Datcu S., Ibos L., Candau Y., Mattei S.: Improvement of building wall Surface temperature measurements by infrared thermography, Infrared Phys. Techn., 46 (2005) 451-467.
  • [24] Bianchi F., Pisello A.L., baldinelli G., Asdrubali F.: Infrared thermography assessment of thermal bridges in building envelope: Experimental validation in a test room setup, Sustainability, 6 (2014) 7107-7120.
Typ dokumentu
Bibliografia
Identyfikator YADDA
bwmeta1.element.baztech-bf99a174-4cc8-4e22-bf79-d69aa9251097
JavaScript jest wyłączony w Twojej przeglądarce internetowej. Włącz go, a następnie odśwież stronę, aby móc w pełni z niej korzystać.