Czasopismo

Archives of Metallurgy and Materials

Tytuł artykułu

Second phase morphology in the Zn-Ti0.1-Cu0.1 single crystals obtained at different growth rates

Autorzy Boczkal, G. 
Treść / Zawartość
Warianty tytułu
PL Morfologia drugiej fazy w monokryształach Zn-Ti0.1-Cu0.1 otrzymywanych przy różnych szybkościach wzrostu
Języki publikacji EN
Abstrakty
EN The influence of growth rate on a morphology, distribution and crystallographic relationship of the intermetallic phase Zn16Ti in Zn-Ti0.1-Cu0.1 single crystals were investigated. The crystals obtained at rates in range of from 1.8mm/h to 16mm/h were tested. In all cases a strong elongation of the Zn16Ti particles along the [11-20] direction is observed. Moreover, it is found that a lamellar phase existing in the crystals develop in range of the growth rate from 6 to 10 mm/h and grows in the f10-11gplanes. In the case of the growth rate of 16mm/h oval-shaped areas of α phase (solid solution of zinc and 0.1wt.% of copper with trace content of titanium) elongated along [10-10] direction and surrounded by needle shaped precipitations are formed in the structure.
PL W pracy badano wpływ szybkości wzrostu monokryształów Zn-Ti0.1-Cu0.1 na morfologię, rozkład i zależności krystalograficzne fazy międzymetalicznej Zn16Ti. Do testów użyto kryształów wyhodowanych z prędkościami z zakresu od 1.8mm/h do 16mm/h. We wszystkich przypadkach zaobserwowano istnienie cząstek tylko jednej fazy Zn,sub>16Ti, wydłużonych na kierunku [11-20]. Ponadto stwierdzono, że przy szybkości wzrostu z zakresu 6 do 10mm/h, obserwowana faza międzymetaliczna ma postać płytkowa, preferująca płaszczyzny wzrostu f10-11g. W przypadku szybkości wzrostu 16mm/h zaobserwowano tworzenie się fazy iglastej, która otacza obszary czystej osnowy (roztwór stały cynku z dodatkiem 0.1% miedzi oraz niewielką zawartością tytanu) tworzące owale wydłużone na kierunku [10-10].
Słowa kluczowe
PL monokryształy   cynk   faza międzymetaliczna  
EN crystal structure   crystal morphology   single crystal growth   zinc compounds  
Wydawca Polish Academy of Sciences, Committee of Metallurgy, Institute of Metallurgy and Materials Science
Czasopismo Archives of Metallurgy and Materials
Rocznik 2012
Tom Vol. 57, iss. 2
Strony 479--484
Opis fizyczny Bibliogr. 16 poz., rys., wykr.
Twórcy
autor Boczkal, G.
  • AGH - University of Science and Technology, Faculty of Non-Ferrous Metals, 30-059 Kraków, 30 Mickiewicza av., Poland
Bibliografia
[1] Von W. Heine, U. Zwicker, Untersuchungen an Legierungen des Systems Zink-Titan, Z. Metallkde. 53, H.6 (1962).
[2] T. Massalski, Binary Alloy Phase Diagrams Second Edition, ASM International (1990).
[3] J.A. Spittle, The Effect of Composition and Cooling Rate on the asCast Microstructure of ZnTi Alloys, Metallography 5, 423-447 (1972).
[4] G. Boczkal, B. Mikułowski, I. Hunsche, C.G. Oertel, W. Skrotzki, Precipitation of intermetallic phase in Zn-Ti alloy single crystals, Cryst. Res.Technol. 43, 2, 135-140 (2008).
[5] G. Boczkal, M. Mikułowski, W. Wołczynski, Oscillatory structure of the Zn-Cu-Ti single crystals, Mat. Sci. Forum 649, 113-118 (2010).
[6] W. Wołczynski, B. Mikułowski, G. Boczkal, Control of the single crystal reinforcement by the intermetallic compound layers, Mat. Sci. Forum 649, 125-130 (2010).
[7] J.A. Spittle, Lamellar and Rod Morphologies in the Zn-TiZn15 Eutectic, Metallography 6, 115-121 (1973).
[8] G.E.R. Schulze, Metallphysik, Akademie-Verlag, Berlin 1974.
[9] G.A. Alers, J.R. Neighbours, The elastic constants of zinc between 4.2and 670K,J. of Phys and Chem of Solids 7, 1, 58-64 October 1958.
[10] C.W. Garland, R. Dalven, Elastic Constants of Zinc from 4.2K to 77.6K, Phys.Rev. 111, 5, Sept. 1 (1958).
[11] M. Saillard, G. Develey, C. Becle, J.M. Moreau, D. Paccard, The Structure of ZnTi16, Act. Cryst. 37B, 224-226 (1981).
[12] P. Mazumder, R. Trivedi, A. Karma, A Model of Convection-Induced Oscillatory Structure Formation in Peritectic Alloys, Metall. and Mat.Trans.A 31A, 1233-1246 (2000).
[13] W.D. Lawson, S. Nielsen, Preparation of Single Crystals. Butterworths Scientific Pub. London (1958).
[14] W.J. Mc.G. Tegart, The electrolytic and chemical polishing of metals in research and industry, 7th edition, Pergamon Press (1959).
[15] B. Mikulowski, G. Boczkal, Zn-Ti single crystals deformed along the basal slip system, Arch.of Met.and Mater. 54, 1, 197 (2009).
[16] B. Mikulowski, Strain Hardening of Zinc Monocrystals with Additions of Silver or Gallium, Metallurgy and Foundry Practice, Scientific Bulletin of Univ. of Mining and Metallurgy 96, Cracow 1982.
Kolekcja BazTech
Identyfikator YADDA bwmeta1.element.baztech-article-BWMA-0025-0010
Identyfikatory