Czasopismo

Fibres & Textiles in Eastern Europe

Tytuł artykułu

Preparation and Characterisation of PSA/CNT Composites and Fibres

Autorzy Chen, Z.  Xin, B.  Wu, X.  Wang, X.  Du, W. 
Treść / Zawartość
Warianty tytułu
PL Wytwarzanie i charakteryzacja kompozytów polisulfonamidowych z udziałem nanorurek węglowych oraz wytworzonych z nich włókien
Języki publikacji EN
Abstrakty
EN In this paper, polysulfonamide/carbon nanotube (PSA/CNT) composite solutions with different CNT contents were prepared using the physical blending method. Corresponding composite fibers were extruded and fabricated through a set of wet spinning units, and composite membranes were prepared by the spin-coating method. The PSA/CNT composite fibers and membranes were characterised by means of SEM, FTIR and XRD among others. The mechanical, thermal and electrical properties were also analysed in this study. The experimental results show that CNT at low contents can be distributed homogeneously in the PSA matrix. Furthermore the molecular structure and chemical composition of PSA does not undergo an obvious change. Crystallisation in the PSA can be promoted at low CNT contents because the nano-particles can act as a nucleation agent. Moreover the electrical conductivity of PSA can be improved significantly by the blending of CNT.
PL Przygotowano szereg zestawów polisulfonamidu i różnej ilości nanorurek węglowych. Z przygotowanego kompozytu wyprodukowano włókna i folie, które zostały scharakteryzowane przez skaningową mikroskopię elektronową, spektroskopię w podczerwieni i dyfrakcję rentgenowską. Analizowano również właściwości mechaniczne, przewodność cieplną i elektryczną otrzymanych próbek. Wyniki wskazują, że przy małym stężeniu nanorurek węglowych mogą one być rozprowadzone jednorodnie w całej matrycy; struktura molekularna i właściwości matrycy PSA nie ulegają zmianie; krystalizacja w matrycy PSA inicjowana jest przez nanorurki; przewodność elektryczna kompozytu zależy w dużym stopniu od ilości dodanych nanorurek.
Słowa kluczowe
PL polysulfonamide   nanorurki węglowe   nanokompozyty   własności termiczne   przewodność elektryczna  
EN polysulfonamide   carbon nanotube   nanocomposites   thermal property   electrical conductivity  
Wydawca Instytut Biopolimerów i Włókien Chemicznych
Czasopismo Fibres & Textiles in Eastern Europe
Rocznik 2012
Tom Nr 5 (94)
Strony 21--25
Opis fizyczny Bibliogr. 14 poz.
Twórcy
autor Chen, Z.
autor Xin, B.
autor Wu, X.
autor Wang, X.
autor Du, W.
  • China, Shanghai, Shanghai University of Engineering Science, College of Fashion
Bibliografia
1. Wang Xiaofeng, Wang Fenghua, Ren Jiarong, et al. The performance and application of PSA fibers. In: Yu Mingfang,The symposium of development and application of high- temperature PSA fibers in 2009 [C]. Shanghai, 2009: 3-7.
2. Wang Jiaming. Development Survey and Market Prospect of Polysulphonamide Fiber. Fine Chemical Industrial Raw Materials & Intermediates 2009; 6-7: 18-24.
3. Ren Jiarong, Wang Xiaofeng, Zhang Yuhua. Development for market and application of polyphenylene sulphonamide fiber. Technical Textiles 2007;25(5): 1-6.
4. Yu Minfeng, Bradley S. Files, Sivaram Arepalli, et al. Tensile loading of ropes of single wall carbon nanotubes and their mechanical properties. Physical Review Letters 2000; 84(24): 5552-5555.
5. Ph. Avouris, J. Appenzeller, R. Martel, et al. Carbon nanotube electronics. In: IEEE, 2003; 91(11): 1772-1784.
6. Zhang Lide, Mou Jimei. The structures of nano materials. Beijing: Science Press, 2001: 420-476.
7. Yang Waitai. The characterization and testing of polymer. Beijing: China Light Industry Press, 2008: 72-80.
8. Meng Qinghao, Hu Jinlian, Zhu Yong. Shape-Memory Polyurethane/Multiwalled Carbon Nanotube Fibers. Journal of Applied Polymer Science 2007; 106:837-848.
9. Liu Jiexia, Tang Zhiyong, Zhang Deren, et al. Preparation and performance of polysulfonamide nanocomposites and it’s fiber [J]. Technical Textiles 2007; 2:14-20.
10. Broadbelt LJ, Dziennik S, aKlein MT. Thermal stability and degradation of aromatic polyamides. Part 2 Structurereactivity relationships in the pyrolysis and hydrolysis of benzamides. Polym Degrad Stab 1994; 45 (1): 57-70.
11. Broadbelt LJ, Dziennik S, Klein MT.Thermal stability and degradation of aromatic polyamides. Part 1 Pyrolysis and hydrolysis pathways, kinetics and mechanisms of N-phenyl benzamide. Polym Degrad Stab 1994; 44 (2): 137-144.
12. Zhang XY, Cheng Y, Zhao. JB. Polymer chemistry. Beijing: China Light Industry Press, 2000: 285.
13. Yang Wantai. Characterization and testing of polymer materials. Beijing: China Light Industry Press, 2008: 144.
14. Jiang Fengdan. Study on the preparation and structure and performance of the Cool polyurethane / CNT nano composites.Beijing: Beijing University of Chemical Technology, 2009.
Kolekcja BazTech
Identyfikator YADDA bwmeta1.element.baztech-article-BPW7-0023-0069
Identyfikatory