Structure and electronic properties of Fe-Ti thin films

Autorzy
Identyfikatory
Warianty tytułu
Języki publikacji
EN
Abstrakty
EN
Fe/Ti multilayers (MLs) prepared onto glass substrates using UHV RF/DC magnetron sputtering. Results showed a significant drop of the coercivity measured for the Fe/Ti MLs with decrease in Fe layer thickness - typically from Hc ~ 2.2 kA/m to Hc ~ 0.2 kA/m - observed at a critical Fe thickness dcrit ~ 2.3 nm. Structural studies showed that the deposition of the 0.18 nm - Fe / 0.22 nm - Ti ML at 285 K leads to the formation of an uniform amorphous Fe-Ti alloy thin film due to a strong interdiffusion during the growth process. On the other hand, in-situ annealing of this ML at 750 K for 2 h resulted in the creation of a nanocrystalline phase. Furthermore, in-situ XPS studies showed that the valence band of the nanocrystalline Fe-Ti alloy film is broader compared to that measured for the amorphous phase with the same average composition.
Rocznik
Strony
827--831
Opis fizyczny
Bibliogr. 12 poz.
Twórcy
autor
autor
  • Institute of Materials Science and Engineering, Poznań University of Technology, pl. M. Skłodowskiej-Curie 5, 60-965 Poznań, smardz@ifmpan.poznan.pl
Bibliografia
  • [1] SMARDZ L., LE DANG K., NIEDOBA H., CHRZUMNICKA K., J. Magn. Magn. Mater., 140–144 (1995), 569.
  • [2] SMARDZ L., Sol. State Comm., 112 (1999), 693.
  • [3] SMARDZ L., SMARDZ K., CZAJKA R., Cryst. Res. Technol., 36 (2001), 1019.
  • [4] SMARDZ L., J. All. Comp., 395 (2005), 17.
  • [5] HERZER G., J. Magn. Magn. Mater., 157/158 (1996), 133.
  • [6] STOBIECKI T., KOPCEWICZ M., CASTAŃO F. J., Chaos, Solitons and Fractals, 10 (1999), 2031.
  • [7] SMARDZ K., SMARDZ L., JURCZYK M., JANKOWSKA E., Phys. Stat. Sol. A, 196 (2003), 263.
  • [8] BOUTEN P. C., MIEDEMA A. R., J. Less Common Metals, 71 (1980), 147.
  • [9] GRIESSEN R., Phys. Rev., B38 (1988) , 3690.
  • [10] SMARDZ L., SMARDZ K., NOWAK M., JURCZYK M., Cryst. Res. Technol., 36 (2001), 1385.
  • [11] SMARDZ L., SMARDZ K., Mol. Phys. Rep., 40 (2004), 137.
  • [12] BRIGGS D., [in:] Handbook of X-ray and Ultraviolet Photoelectron Spectroscopy, D. Briggs (Ed.), Heyden and Son Ltd., London, 1977, p. 153 and references therein.
Typ dokumentu
Bibliografia
Identyfikator YADDA
bwmeta1.element.baztech-article-BPW1-0021-0046
JavaScript jest wyłączony w Twojej przeglądarce internetowej. Włącz go, a następnie odśwież stronę, aby móc w pełni z niej korzystać.