Week interlayer exchange coupling in Fe-Zr and Fe-Ti layered structures

Autorzy
Identyfikatory
Warianty tytułu
Języki publikacji
EN
Abstrakty
EN
20nm-Fe/dZr-Zr/20nm-Fe and 20nm-Fe/dTi-Ti/20nm-Fe trilayers with wedged Zr and Ti sublayers were prepared at room temperature using UHV (5 × 10-10 mbar) RF/DC magnetron sputtering. Results showed that the Fe sublayers are ferromagnetically coupled up to Zr and Ti spacer thickness of about 1.5 and 2 nm, respectively. Furthermore, a weak antiferromagnetic (ferromagnetic) coupling of the Fe sublayers was observed for a Zr (Ti) thickness range between 1.5 and 3 nm (2 and 3.4 nm). The Fe sublayers are very weakly exchange coupled or decoupled for dZr > 3 nm and dTi > 3.4 nm. The small decoupling Ti and Zr thickness could be explained by spontaneous formation of a quasi-amorphous structure of the paramagnetic spacer during the deposition process.
Rocznik
Strony
821--826
Opis fizyczny
Bibliogr. 10 poz.
Twórcy
autor
autor
Bibliografia
  • [1] SMARDZ L., Sol. State Comm., 112 (1999), 693.
  • [2] SMARDZ L., Czech. J. Phys., 52 (2002), 209.
  • [3] BÜRGLER D.E., SCHALLER D.M., SCHMIDT C.M., MEISINGER F., KROHA J., MCCORD J., HUBERT A., GÜNTHERODT H.J., Phys. Rev. Lett., 80 (1998), 4983.
  • [4] SMARDZ L., SMARDZ K., Mol. Phys. Rep., 40 (2004), 137.
  • [5] SMARDZ L., J. All. Comp., 389 (2005), 17.
  • [6] SMARDZ K., SMARDZ L., Mater. Sci.-Poland, 24 (2006), 827.
  • [7] SAMWER K., Phys. Reports ,161 (1988), 3.
  • [8] STOBIECKI T., KOPCEWICZ M., CASTAŇO F.J., Chaos, Solitons and Fractals, 10 (1999), 2031.
  • [9] SMARDZ K., PhD Thesis, Institute of Molecular Physics, Polish Acad. Sci., Poznań (Poland), 1999. [10] BRIGGS D., [in:] Handbook of X-ray and Ultraviolet Photoelectron Spectroscopy, D. Briggs (Ed.), Heyden & Son Ltd., London, 1977, p. 153 and references therein.
Typ dokumentu
Bibliografia
Identyfikator YADDA
bwmeta1.element.baztech-article-BPW1-0021-0045
JavaScript jest wyłączony w Twojej przeglądarce internetowej. Włącz go, a następnie odśwież stronę, aby móc w pełni z niej korzystać.