The influence of temperature on selected strength properties of furniture particleboard

• Autorzy: Borysiuk Piotr , Tetelewska Anna , Auriga Radosław , Jenczyk-Tołłoczko Izabella

Identyfikatory

DOI

10.5604/01.3001.0013.7697

• Języki publikacji: EN

Abstrakty

EN

The influence of temperature on selected strength properties of furniture particleboard. As a part of the study, the influence of temperature on selected properties of furniture particleboard was tested. P2 type industrial particleboards in three finishing options: raw boards (1), boards covered with melamine film in white (2) and black (3) (10 samples per variant) have been subjected to temperatures from -20oC to +120oC, at 10oC intervals. The Time of exposure for individual temperatures was 7 days. MOR, MOE and IB were determined for tested boards. It has been shown that temperatures above 50oC have a negative effect on strength properties of boards. A large decrease in all tested parameters was observed in the temperature range from +60oC to +120oC. It was also noted that finishing boards with melamine film did not improve their durability.

PL

Wpływ temperatury na wybrane właściwości wytrzymałościowe meblowych płyt wiórowych. W ramach pracy zbadano wpływ temperatury na wybrane właściwości meblowych płyt wiórowych. Przemysłowe płyty wiórowe typu P2 w trzech wariantach wykończenia: płyty surowe (1), płyty pokryte filmem melaminowym w kolorze białym (2) i w kolorze czarnym (3) (po 10 próbek na wariant) zostały poddane działaniu temperatur od -20oC do +120oC, z od stopniowaniem, co 10 K. Czas oddziaływania poszczególnych temperatur wynosił 7 dni. Dla badanych płyt oznaczono MOR, MOE. IB, odporności laminatu na pękanie. Wykazano, że temperatura powyżej +50oC wywiera negatywny wpływ na właściwości wytrzymałościowe płyt. Zaobserwowano duży spadek wszystkich badanych parametrów w przedziale temperatur od +60oC do +120oC. Stwierdzono również, że wykończenie płyt filmem melaminowym nie wpływa na poprawę ich wytrzymałości.

Słowa kluczowe

EN

furniture particleboard; temperature; strength properties

• Wydawca: Wydawnictwo Szkoły Głównej Gospodarstwa Wiejskiego w Warszawie
• Czasopismo: Annals of Warsaw University of Life Sciences - SGGW. Forestry and Wood Technology
• Rocznik: 2019
• Tom: No. 108
• Strony: 128--134
• Opis fizyczny: Bibliogr. 19 poz., rys., tab.

Twórcy

autor

Borysiuk Piotr

• Institute of Wood Sciences and Furniture, Warsaw University of Life Sciences – SGGW, 159 Nowoursynowska St., 02-787 Warsaw

autor

Tetelewska Anna

• Institute of Wood Sciences and Furniture, Warsaw University of Life Sciences – SGGW, 159 Nowoursynowska St., 02-787 Warsaw

autor

Auriga Radosław

• Institute of Wood Sciences and Furniture, Warsaw University of Life Sciences – SGGW, 159 Nowoursynowska St., 02-766 Warsaw

autor

Jenczyk-Tołłoczko Izabella

• Institute of Wood Sciences and Furniture, Warsaw University of Life Sciences – SGGW, 159 Nowoursynowska St., 02-787 Warsaw

Bibliografia

• 1. AYRILMIS N., BUYUKSARI U., AS N., 2010: Bending strength and modulus ofelasticity of wood-based panels at cold and moderate temperatures. Cold RegionsScience and Technology 63, pp. 40–43.
• 2. BAUMANN R., 1922: Die bisherigen Ergebnisse der Holzprüfungen in der Materialprüfungsanstalt an der Technischen Hochschule Stuttgart. Heft 231 derForschungsarbeiten auf dem Gebiete des Ingenieurwesens. Berlin.
• 3. BEKHTA P., ŁĘCKA J., MORZE Z., 2003: Short-term effect of the temperature onthe bending strength of wood-based panels. Holz als Roh- und Werkstof 61, pp. 423–424.
• 4. BORYSIUK P., KOZAKIEWICZ P., NURCZYK T., 2018: Wpływ temperatury nawybrane właściwości płyt wiórowych. Biuletyn Informacyjny Ośrodka Badawczo-Rozwojowego Przemysłu Płyt Drewnopochodnych w Czarnej Wodzie, 1/2, pp. 6–13.
• 5. EN 310:1994 Wood-based panels. Determination of modulus of elasticity in bendingand of bending strength.
• 6. EN 312:2010 Particleboards. Specifications.
• 7. EN 319:1999 Particleboards and fibreboards. Determination of tensile strength perpendicular to the plane of the board.
• 8. GREEN D.W., WINANDY J.E., KRETSCHMANN D.E., 1999: Mechanical Properties of Wood – Chapter 4 in: Wood handbook – wood as an engineering material. Forest Products Laboratory USDA Forest Service. Madison, Wisconsin USA.
• 9. HIRATA T., KAWAMOTO S., OKURO A., 1991: Pyrolysis of Melamine –Formaldehyde and Urea – Formaldehyde Resins. J. Appl. Polym. Sci., 42.
• 10. http://www.fao.org/faostat/en/#data/FO (electronic document, as of November 10,2019)
• 11. https://businessinsider.com.pl/wiadomosci/produkcja-mebli-w-polsce-w-i-kwartale-2019-roku/5z8480v (electronic document, as of November 05, 2019).
• 12. KOLLMANN F., 1940: Die mechanischen Eigenschaften verschieden feuchter Hölzerim Temperaturbereich von –200 bis + 200 oC. Forschung auf dem Gebiete desIngenieurwesens 403 (11), pp. 1–18. VDI-Verlag. Berlin.
• 13. KOLLMANN F., 1942: Über das Gefrieren und den Einfluß tiefer Temperaturen auf die Festigkeit der Hölzer. Mitteilungen der Hermann-Göring-Akademie der Deutschen Forstwissenschaft. 2. Jahrgang, Band 1. J.D. Sauerländer Verlag. Fankfurt am Mein.
• 14. KOZAKIEWICZ P., 2010: Wpływ temperatury i wilgotności na wytrzymałość naściskanie wzdłuż włókien wybranych rodzajów drewna o zróżnicowanej gęstościi budowie anatomicznej. Trzysta siedemdziesiąta pozycja serii - Rozprawy Naukowei Monografie Wydawnictwo SGGW, Warszawa.
• 15. KOZAKIEWICZ P., MATEJAK M., 2013: Klimat a drewno zabytkowe - dawnai współczesna wiedza o drewnie. Wydanie IV – zmienione. Wydawnictwo SGGW.Warszawa.
• 16. KULMAN S., BOIKO L., ANTSYFEROVA A., 2015: Bending strength (modulus ofrupture) and modulus of elasticity of MDF different density at various temperature,Annals of Warsaw University of Life Sciences Forestry and Wood Technology, 91:pp. 101–106
• 17. SONDEREGGER W., NIEMZ P., 2006: Der Einfluss der Temperatur auf die Biegefestigkeit und den Elastizitäts modul bei verscheidenen Holzwerkstoffen. Holzals Roh- und Werkstoff 64, pp. 385–591.
• 18. VORREITER L., 1938: Biege- und Druckfestigeit gefrorenen Fichtenholzes.Tharandter Forestl. Jahrbuch Bd. 89: pp. 491–510.
• 19. www.biznesmeblowy.pl/rynek_mebli/111/jaki_byl_rok_2018_w_branzy_meblarskiej_zobacz_najnowszy_raport,16390.html (electronic document, as of November 5,2019).