Properties of GdFeAl ternary compound in two crystallographic structures

Identyfikatory
Warianty tytułu
Języki publikacji
EN
Abstrakty
EN
Properties of the GdFeAl compound which crystallized in the cubic MgCu2-type structure as well as in hexagonal MgZn2-type structure were compared. The electrical resistivity, AC susceptibility and magnetization as a function of temperature revealed relatively high magnetic ordering temperature about 200 K. The differences in magnetization were observed for samples crystallizing in two different crystallographic structures. The magnetic moments measured at 4.2 K and up to140 kOe are very far from the magnetic moment value for free Gd ion. The magnetic moment values of cubic and hexagonal phases are 1.1 μB and 1.7μB, respectively.
Rocznik
Strony
954--958
Opis fizyczny
Bibliogr. 14 poz., tab., wykr.
Twórcy
autor
  • Institute of Physics, University of Silesia, Uniwersytecka 4, 40-007 Katowice, Poland
autor
  • Institute of Physics, University of Silesia, Uniwersytecka 4, 40-007 Katowice, Poland
autor
  • Institute of Physics, University of Silesia, Uniwersytecka 4, 40-007 Katowice, Poland
autor
Bibliografia
  • [1] YU B.F.,GAO Q.,ZHANG B.,MENG X.Z., CHEN Z., Int. J. Refrigeration, 26 (2003), 622.
  • [2] PECHARSKY V.K., GSCHNEIDER JR K.A., J. Appl. Phys., 85 (1999), 5365.
  • [3] GSCHNEIDER JR K.A., PECHARSKY V.K., Annu. Rev. Mater. Sci., 30 (2000), 387
  • [4] GSCHNEIDNER JR K.A.,PECHARSKY V.K., TSOKOL A.O., Rep. Prog. Phys., 68 (2005), 1479.
  • [5] BRÜCK E.,J. Phys. D Appl. Phys., 38 (2005), R381.
  • [6] NAPOLETANO M.,CANEPA F.,MANFRINETTI P., MERLO F.,J. Mater. Chem., 10 (2000), 1663.
  • [7] HULLIGER F., J. Alloys Comp., 218 (1995), 44.
  • [8] TSVYASHCHENKO A.V., FOMICHEVA L.M., J. Less Common Met., 135 (1987), L9.
  • [9] TALIK E., KUSZ J., HOFMEISTER W., MATLAK M., SKUTECKA M., KLIMCZAK M., J. Alloys Comp., 423 (2006), 47.
  • [10] ŚLEBARSKI A., J. Magn. Magn. Mater., 66 (1987), 107.
  • [11] BUSCHOW K.H.J., J. Magn. Magn. Mater., 38 (1983), 91.
  • [12] OESTERREICHER H., J. Less Common Met., 13 (1967), L9.
  • [13] JAROSZ J., TALIK E., MYDLARZ T., KUSZ J., BÖHM H., WINIARSKI A., J. Magn. Magn. Mater., 208 (2000), 169.
  • [14] JAROSZ J.,TALIK E.,J. Alloys Compounds, 317 (2001), 385.
Typ dokumentu
Bibliografia
Identyfikator YADDA
bwmeta1.element.baztech-320ae41b-ce24-40f3-88f0-e09c2dcc78a6
JavaScript jest wyłączony w Twojej przeglądarce internetowej. Włącz go, a następnie odśwież stronę, aby móc w pełni z niej korzystać.